中密度ポリエチレンの疲労き裂進展と過負荷効果に関する実験的研究【JST・京大機械翻訳】

Experimental Study on the Fatigue Crack Growth and Overload Effect in Medium Density Polyethylene

著者 (4件)： Qian Yang-fan (State Key Laboratory of Ocean Engineering, School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiao Tong University, Shanghai, China) ,  Yang Feng-peng (State Key Laboratory of Ocean Engineering, School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiao Tong University, Shanghai, China) ,  He Hou-feng (State Key Laboratory of Ocean Engineering, School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiao Tong University, Shanghai, China) ,  Du He-yang (State Key Laboratory of Ocean Engineering, School of Naval Architecture, Ocean and Civil Engineering, Shanghai Jiao Tong University, Shanghai, China)
資料名： Journal of Materials Engineering and Performance  (Journal of Materials Engineering and Performance)
巻： 29  号： 10  ページ： 6681-6690  発行年： 2020年 
JST資料番号： C0161B  ISSN： 1059-9495  CODEN： JMEPEG  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 一定振幅荷重下の中密度ポリエチレン(MDPE)の疲れ亀裂成長挙動を板試験片上で実験した。付加した単一過負荷の効果も調べた。疲れ亀裂成長における高分子材料の実際の亀裂フロント形状を得るために,最適化亀裂フロントマーキング法を開発し,それを,研究したMDPEに首尾よく適用した。結果は,疲労亀裂成長の遅れが,引張過負荷が適用された後に明らかに現れ,それは金属材料と類似していたことを示した。ウェッジ型塑性ゾーンの不動態化は亀裂遅延の主因であった。残留応力に基づく理論は,遅れ影響を説明するために導入して,亀裂先端の塑性区域サイズは,Dugdaleモデルによって計算した。Wheelerモデルを用いて亀裂成長速度の低下を当てはめた。Copyright ASM International 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 塑性 ,  亀裂 ,  最適化 ,  残留応力 ,  金属材料 ,  *ポリエチレン ,  不動態化 ,  引張 ,  過負荷 ,  中密度ポリエチレン ,  亀裂先端 ,  *疲れ亀裂成長
準シソーラス用語： 高分子材料 ,  亀裂伝搬速度 , 【Automatic Indexing@JST】

著者キーワード (5件)： 疲労亀裂成長 ,  破壊表面 ,  過負荷 ,  ポリエチレン ,  Wheelerモデル

分類 (2件)： 金属材料  (HC05020S) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 中密度ポリエチレン ,  疲労き裂進展 ,  過負荷 ,  実験的研究