0.5Tm以下の温度で達成したMnリッチ高強度鋼の異常な温間延性【JST・京大機械翻訳】

Extraordinary warm ductility of a Mn-rich high-strength steel achieved at temperature below 0.5 T_m

著者 (5件)： Cheng Guan-Ju (Department of Materials Science and Engineering, National Taiwan University, Roosevelt Road, Taipei, Taiwan, Republic of China) ,  Lai Zen-Hao (Department of Materials Science and Engineering, National Taiwan University, Roosevelt Road, Taipei, Taiwan, Republic of China) ,  Jia Tao (The State Key Lab of Rolling and Automation, Northeastern University, Shenyang, Liaoning Province, People’s Republic of China) ,  Huang Ching-Yuan (Iron and Steel R&D Department, China Steel Corporation, Chung Kang Road, Kaohsiung, Taiwan, Republic of China) ,  Yen Hung-Wei (Department of Materials Science and Engineering, National Taiwan University, Roosevelt Road, Taipei, Taiwan, Republic of China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 803  ページ： Null  発行年： 2021年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究は,Mnリッチ高強度鋼における0.5T_m以下の温度(融点)で大きな延性を達成するために変形中のオーステナイト反転を採用した。この目標をAlの無いMnリッチ鋼で達成し,0.5T_m以下のより高いオーステナイト反転速度を得た。引張結果は,550°Cで90%以上の異常な延性を示し,それは鋼の約0.48T_mである。熱力学計算を適用してAlと歪エネルギーの影響を明らかにした。さらに,電子後方散乱回折を用いて,種々の条件下で微細構造進展を調べた。オーステナイト変態速度は,温間変形中の延性向上におけるフェライト再結晶より重要であることが分かった。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *延性 ,  塑性 ,  再結晶 ,  フェライト ,  アルミニウム ,  *鋼 ,  オーステナイト ,  融点 ,  引張 ,  歪エネルギー ,  *高強度鋼
準シソーラス用語： オーステナイト化 ,  EBSD ,  微細構造進展 ,  温間変形 , 【Automatic Indexing@JST】

著者キーワード (5件)： 温間延性 ,  オーステナイトの復帰 ,  超微粒子 ,  変換 ,  温間温度塑性