熱電池用の高比容量カソードとしてのフレキシブルなNiS_2膜【JST・京大機械翻訳】

Flexible NiS₂ film as high specific capacity cathode for thermal battery

著者 (7件)： Bin Yao (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Fu Licai (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Liao Zheng (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Zhu Jiajun (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Yang Wulin (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Li Deyi (College of Materials Science and Engineering, Hunan University, Changsha 410082, China) ,  Zhou Lingping (College of Materials Science and Engineering, Hunan University, Changsha 410082, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 900  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 粉体プレス技術は,熱電池のカソードを調製するための普遍的な手段として考えられている。本研究では,厚さ120μmのフレキシブルNiS_2膜カソードをテープキャスティング法により調製した。それは,高温での有機接着剤破壊の問題を克服した。NiS_2膜は350°Cでの熱処理後に同等の延性を保持した。そして,亀裂は100回の曲げの後,膜表面に発生しなかった。その密度はNiS_2錠剤と類似している。単一熱電池において,250mA cm-2で648mA h g-1の超高比容量を1.5Vのカットオフ電圧で達成できた。その短いリチウムイオン透過距離のため,比容量はNiS_2錠剤と比較して13%増加した。本研究は,フルコンポーネントフレキシブル熱電池に関する研究の参照意義を与える。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  亀裂 ,  高温 ,  熱処理 ,  粉体 ,  接着剤 ,  *静電容量 ,  リチウム化合物 ,  臨界電圧 ,  *カソード
準シソーラス用語： テープ成形 ,  リチウムイオン ,  *比容量 , 【Automatic Indexing@JST】

著者キーワード (4件)： 熱電池 ,  NiS_2膜 ,  フレキシブルカソード ,  高い比容量

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (3件)： 熱電池 ,  比容量 ,  カソード