4熱間圧延ミルにおけるバイメタルロールの疲れ破壊リスク評価【JST・京大機械翻訳】

Fatigue failure risk evaluation of bimetallic rolls in four-high hot rolling mills

著者 (6件)： Aridi Mohd Radzi (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan) ,  Noda Nao-Aki (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan) ,  Sano Yoshikazu (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan) ,  Takata Kakeru (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan) ,  Sun Zifeng (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan) ,  Takase Yasushi (Department of Mechanical Engineering, Kyushu Institute of Technology, Kitakyushu-shi, Japan)
資料名： Fatigue & Fracture of Engineering Materials & Structures  (Fatigue & Fracture of Engineering Materials & Structures)
巻： 45  号： 4  ページ： 1065-1087  発行年： 2022年 
JST資料番号： H0708A  ISSN： 8756-758X  CODEN： FFESEY  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 熱間圧延機では,高速鋼(HSS)と延性鋳造鉄(DCI)を適用することで,優れた硬度と耐摩耗性のため,バイメタルロールを使用する。これまでの研究の大部分は表面スポーリングに焦点を合わせているので,圧延中の応力に基づく内部疲れ破壊についてはほとんど研究がない。本研究では,三次元有限要素法を適用して,4高圧延機におけるワークロールの圧延応力を調べた。バックアップロールにおける適切なシャムファー形状を,疲れに及ぼすそれらの影響を考慮することによって,標準摩耗プロファイルと同様に議論した。次に,圧縮平均応力下の疲労リスクを評価するために,応力振幅対平均応力線図の疲れ限界線を新たに考察した。産業における以前の経験の助けにより,疲労破壊リスクを,ワークロール内部の3つの臨界点に焦点を当てて議論した。Copyright 2022 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  応力 ,  摩耗 ,  *バイメタル ,  高速度鋼 ,  鋳造 ,  *圧延 ,  圧延機 ,  *熱間圧延 ,  スポーリング ,  平均応力 ,  疲れ強さ ,  *疲れ破壊 ,  ワークロール ,  バックアップロール

著者キーワード (5件)： バイメタルロール ,  疲労破壊 ,  4段圧延機 ,  ロールプロファイル ,  応力解析