超軽量泡ガラスの製造における発泡添加剤と使用速度の研究【JST・京大機械翻訳】

An investigation of foaming additives and usage rates in the production of ultra-light foam glass

著者 (6件)： Davraz M. (Senirkent Vocational School, Department of Construction, Isparta University of Applied Science, Isparta, Turkey) ,  Koru M. (Technology Faculty, Department of Mechanical Engineering, Isparta University of Applied Science, Isparta, Turkey) ,  Akdag A. E. (Vocational School of Technical Science, Isparta University of Applied Science, Isparta, Turkey) ,  Kilincarslan S. (Engineering Faculty, Department of Civil Engineering, Suleyman Demirel University, Isparta, Turkey) ,  Delikanli Y. E. (Senirkent Vocational School, Department of Machinery, Isparta University of Applied Science, Isparta, Turkey) ,  Cabuk M. (Faculty of Engineering, Department of Metallurgy and Materials, Mersin University, Mersin, Turkey)
資料名： Journal of Thermal Analysis and Calorimetry  (Journal of Thermal Analysis and Calorimetry)
巻： 147  号： 5  ページ： 3567-3576  発行年： 2022年 
JST資料番号： H0095C  ISSN： 1388-6150  CODEN： JTHEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,廃ガラス粉末から粒径<150μmまでの見かけの密度<200kgm-3を有する発泡ガラスの製造可能性を調べた。本研究では,廃棄物窓ガラスおよび廃ソーダボトルから得たガラス粉末を充填剤として用い,ケイ酸ナトリウム,炭化ケイ素,酸化マンガン,炭酸カルシウム,活性炭およびグリセリンを発泡剤として用いた。試料を875°C,25分間,灰オーブン中で焼結し,次に10°C/minで冷却した。得られた発泡ガラス試料の体積を測定し,それらの質量を精密尺度で測定し,次にそれらの密度を計算した。試料の細孔径とモルフォロジーを走査電子顕微鏡(SEM)で調べた。発泡ガラス試料の圧縮強度を試験し,それらの熱伝導率係数を熱流計法を用いて測定した。その結果,廃ガラスの化学構造,発泡添加剤の最適量およびそれらの比率を,超軽量発泡ガラスの製造に対して決定した。Copyright Akademiai Kiado, Budapest, Hungary 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *ガラス ,  焼結 ,  走査電子顕微鏡 ,  熱伝導率 ,  粉体 ,  炭酸カルシウム ,  ケイ酸ナトリウム ,  酸化マンガン ,  炭化ケイ素 ,  発泡剤 ,  *泡ガラス ,  *起泡 ,  圧縮強さ ,  モルフォロジー
準シソーラス用語： 廃ガラス , 【Automatic Indexing@JST】

著者キーワード (5件)： 泡ガラス ,  廃ガラス粉末 ,  発泡添加剤 ,  密度 ,  熱伝導率