製鋼スラグコンクリートの圧縮強度と吸水に及ぼすアルカリ活性化剤量の影響【JST・京大機械翻訳】

The impact of alkali activator dosage on the compressive strength and water absorption of steel slag concrete

著者 (5件)： Ho Chia Min (Department of Civil Engineering, College of Engineering, Universiti Malaysia Pahang, 26300 Gambang, Kuantan, Pahang, Malaysia) ,  Doh Shu Ing (Department of Civil Engineering, College of Engineering, Universiti Malaysia Pahang, 26300 Gambang, Kuantan, Pahang, Malaysia) ,  Mohammad Al-Btoush A.K.A. (Isra University Office, Amman PO Box 33 and 22, 11622 Amman, Jordan) ,  Li XiaoFeng (Department of Civil Engineering, College of Engineering, Universiti Malaysia Pahang, 26300 Gambang, Kuantan, Pahang, Malaysia) ,  Chin Siew Choo (Department of Civil Engineering, College of Engineering, Universiti Malaysia Pahang, 26300 Gambang, Kuantan, Pahang, Malaysia)
資料名： Materials Today: Proceedings  (Materials Today: Proceedings)
巻： 51  号： P2  ページ： 1323-1326  発行年： 2022年 
JST資料番号： W3531A  ISSN： 2214-7853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 鋼スラグ(SS)はコンクリートのセメント置換の代替である。しかし,SSの高い置換率は,コンクリートの初期強度を低下させると同時にコンクリートのワーカビリティを増加させる。本研究の目的は,セメント置換材として40%SSを含むコンクリート中のアルカリ活性化剤の,そのワーカビリティ,圧縮強度,および吸水率に対する効果を調べることである。本研究では,異なる量のNa_2SO_4を,40%の固定セメント置換率でSSベースコンクリートに添加した。結果は,SSベースコンクリートのワーカビリティがNa_2SO_4添加量の増加とともに減少することを示した。初期強度はNa_2SO_4の1から3%への添加と共に増加し,3%以上減少した。28日と90日の強度はNa_2SO_4の1から4%への添加で増加し,4%以上減少した。SSベースコンクリートの吸水率は,Na_2SO_4の増加とともに著しく減少した。実験結果から,4%Na_2SO_4の添加が28日で35.12MPaの最高強度を与えることが観察された。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： セメント ,  *添加剤 ,  *コンクリート ,  吸水 ,  硫酸ナトリウム ,  *圧縮強さ ,  ワーカビリティ ,  *製鋼スラグ ,  置換 ,  吸水率 ,  置換率
準シソーラス用語： *活性化剤 ,  初期強度 ,  添加量 , 【Automatic Indexing@JST】

著者キーワード (4件)： 圧縮強度 ,  製鋼スラグ ,  硫酸ナトリウム ,  水の吸収

分類 (1件)： モルタル,コンクリート  (RA06042H)

タイトルに関連する用語 (6件)： 製鋼スラグ ,  コンクリート ,  圧縮強度 ,  吸水 ,  アルカリ ,  活性化剤