鋳放しH13鋼の微細組織と微小硬さに及ぼす均質化温度の影響【JST・京大機械翻訳】

Effect of Homogenisation Temperature on the Microstructure and Microhardness of As-Cast H13 Steel

著者 (6件)： Han Yahui (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China) ,  Li Changsheng (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China) ,  He Shuai (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China) ,  Gao Cairu (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China) ,  Chen Shuaishuai (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China) ,  Li En (State Key Lab of Rolling and Automation, Northeastern University, Shenyang, People’s Republic of China)
資料名： Metals and Materials International  (Metals and Materials International)
巻： 28  号： 3  ページ： 755-769  発行年： 2022年 
JST資料番号： W0990A  ISSN： 1598-9623  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,鋳放しH13鋼の均質化温度範囲は1150から1230°Cであり,一方,均質化温度範囲がミクロ組織の変化と微小硬さに及ぼす影響を試験した。デンドライト偏析領域における合金元素の濃縮はマトリックスの固相線温度を低下させ,その全含有量は最大均質化温度を決定した。二次デンドライト枝は1150°Cで最も溶解し,過熱は偏析領域で1230°Cに現れた。さらに,一次炭化物は収縮,不動態化,フラグメンテーションおよび溶解を受けた。二次炭化物M_23C_6とM_6Cは,それぞれMC/γとM_7C_3/γの界面に形成された。均質化温度が1150から1230°Cに上昇すると,微小硬さの値は771から740HVに徐々に低下した。それにもかかわらず,標準偏差値は最初に減少し,次に増加し,1200°Cで最小32HVに達し,硬度均一性が最良であることを示した。Copyright The Korean Institute of Metals and Materials 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  *微小硬さ ,  偏析 ,  標準偏差 ,  金属組織 ,  炭化物 ,  不動態化 ,  合金元素 ,  樹枝状結晶 ,  均質化 ,  フラグメンテーション ,  固相線 ,  *鋳放し
準シソーラス用語： 温度範囲 ,  AISIH13 , 【Automatic Indexing@JST】

著者キーワード (5件)： 鋳放しH13鋼 ,  均質化温度 ,  デンドライト分離 ,  一次炭化物 ,  微小硬さ