厚み可変強磁性を有する空気安定2D Cr_5Te_8ナノシート【JST・京大機械翻訳】

Air-Stable 2D Cr₅Te₈ Nanosheets with Thickness-Tunable Ferromagnetism

著者 (13件)： Chen Chao (Key Laboratory of Applied Surface and Colloid Chemistry (Ministry of Education), Shaanxi Key Laboratory for Advanced Energy Devices, School of Materials Science and Engineering, Shaanxi Normal University, Xi’an, 710119, P. R. China) ,  Chen Xiaodie (Wuhan National High Magnetic Field Centre, Department of Physics, Huazhong University of Science and Technology, Wuhan, 430074, P. R. China) ,  Wu Changwei (Shenzhen Key Laboratory of Nanobiomechanics, Shenzhen Institutes of Advanced Technology, Chinese Academy of Sciences, Shenzhen, Guangdong, 518055, P. R. China) ,  Wang Xiao (Shenzhen Key Laboratory of Nanobiomechanics, Shenzhen Institutes of Advanced Technology, Chinese Academy of Sciences, Shenzhen, Guangdong, 518055, P. R. China) ,  Ping Yue (Key Laboratory of Applied Surface and Colloid Chemistry (Ministry of Education), Shaanxi Key Laboratory for Advanced Energy Devices, School of Materials Science and Engineering, Shaanxi Normal University, Xi’an, 710119, P. R. China) ,  Wei Xin (Key Laboratory of Applied Surface and Colloid Chemistry (Ministry of Education), Shaanxi Key Laboratory for Advanced Energy Devices, School of Materials Science and Engineering, Shaanxi Normal University, Xi’an, 710119, P. R. China) ,  Zhou Xing (State Key Laboratory of Material Processing and Die & Mould Technology, School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan, 430074, P. R. China) ,  Lu Jiangbo (School of Physics and Information Technology, Shaanxi Normal University, Xi’an, 710119, P. R. China) ,  Zhu Lujun (School of Physics and Information Technology, Shaanxi Normal University, Xi’an, 710119, P. R. China) ,  Zhou Jiadong (Key Lab of Advanced Optoelectronic Quantum Architecture and Measurement (Ministry of Education), School of Physics, Beijing Institute of Technology, Beijing, 100081, P. R. China) ,  Zhai Tianyou (State Key Laboratory of Material Processing and Die & Mould Technology, School of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan, 430074, P. R. China) ,  Han Junbo (Wuhan National High Magnetic Field Centre, Department of Physics, Huazhong University of Science and Technology, Wuhan, 430074, P. R. China) ,  Xu Hua (Key Laboratory of Applied Surface and Colloid Chemistry (Ministry of Education), Shaanxi Key Laboratory for Advanced Energy Devices, School of Materials Science and Engineering, Shaanxi Normal University, Xi’an, 710119, P. R. China)
資料名： Advanced Materials  (Advanced Materials)
巻： 34  号： 2  ページ： e2107512  発行年： 2022年 
JST資料番号： W0001A  ISSN： 0935-9648  CODEN： ADVMEW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 2D磁性材料は,スピントロニクスデバイスにおける有望な応用のため,広範な研究関心を喚起した。しかし,より良い安定性を持ち,それらのバッチ合成を実現する新しい種類の2D磁性材料の探索は,依然として困難である。ここでは,チューブインチューブ化学蒸着(CVD)成長技術による調整可能な厚さを有する空気安定性2D Cr_5Te_8超薄結晶の合成を報告した。チューブインチューブCVD成長の重要性は,分解方向への平衡シフトを著しく抑制し,正確な組成を有する高品質Cr_5Te_8の合成に対して,合成反応方向への促進を可能にする。成長温度を正確に調整することによって,Cr_5Te_8ナノシートの厚さは,三角形から六角形へ変化する形態で,≒1.2nmから数十nmまで調整される。さらに,磁気光学Kerr効果測定は,Cr_5Te_8ナノシートが強い面外スピン分極を有する強磁性であることを明らかにした。Curie温度は,Cr_5Te_8厚さが10から30nmに増大すると,100から160Kへ単調な増加を示し,空気暴露後,表面粗さや磁気特性に明らかな変化は無かった。本研究は,高品質の2D強磁性材料の制御可能な合成のためのロバストな方法を提供し,スピントロニクスにおける研究進展を促進するであろう。Copyright 2022 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Curie温度 ,  *強磁性 ,  磁気的性質 ,  磁性材料 ,  スピン分極 ,  *二次元 ,  化学蒸着 ,  ロバスト性 ,  スピントロニクス ,  *ナノシート
準シソーラス用語： 高品質 , 【Automatic Indexing@JST】

著者キーワード (5件)： 2D材料 ,  Cr_5Te_8 ,  CVD成長 ,  強磁性 ,  調整可能な厚さ

分類 (2件)： 無機化合物一般及び元素  (CD01010D) ,  金属酸化物及び金属カルコゲン化物の結晶構造  (BK07020Y)

タイトルに関連する用語 (4件)： 厚み ,  可変 ,  強磁性 ,  2D