人工海水中におけるTi-6Al-3Nb-2Zr-1Mo合金の不動態化挙動に及ぼす温度と溶存酸素の影響【JST・京大機械翻訳】

Effect of temperature and dissolved oxygen on the passivation behavior of Ti-6Al-3Nb-2Zr-1Mo alloy in artificial seawater

著者 (6件)： Li Xiaoqi (College of Mechanical and Electrical Engineering, Qingdao University, Qingdao, 266071, China) ,  Li Xiaoqi (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute (LSMRI), Qingdao, 266101, China) ,  Wang Liwei (College of Mechanical and Electrical Engineering, Qingdao University, Qingdao, 266071, China) ,  Fan Lin (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute (LSMRI), Qingdao, 266101, China) ,  Cui Zhongyu (School of Materials Science and Engineering, Ocean University of China, Qingdao, 266100, China) ,  Sun Mingxian (State Key Laboratory for Marine Corrosion and Protection, Luoyang Ship Material Research Institute (LSMRI), Qingdao, 266101, China)
資料名： Journal of Materials Research and Technology  (Journal of Materials Research and Technology)
巻： 17  ページ： 374-391  発行年： 2022年 
JST資料番号： W3532A  ISSN： 2238-7854  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 人工海水中のTi-6Al-3Nb-2Zr-1Mo合金の不動態化挙動に及ぼす温度と溶存酸素の影響を調べた。温度の上昇は,陽極と陰極電流密度を増加させ,また,酸素空孔運動に対する電界強度とゼロ磁場活性化エネルギーを増加させた。溶存酸素濃度の減少は酸化チタンの変換を阻害し,陽極ピークの消失をもたらした。一方,点欠陥密度と拡散速度の増加のため,脱気環境において不動態電流密度は増加した。不動態膜はn型半導体を示し,酸素空孔は主な点欠陥であった。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 活性化エネルギー ,  *合金 ,  磁場 ,  *不動態 ,  *不動態化 ,  不動態皮膜 ,  *溶存酸素 ,  酸化チタン ,  電流密度 ,  拡散速度 ,  電界強度 ,  アノード ,  カソード
準シソーラス用語： 酸素空格子点 , 【Automatic Indexing@JST】

著者キーワード (4件)： チタン合金 ,  EIS ,  不動態化 ,  電気化学挙動

分類 (3件)： 腐食  (WB03030B) ,  電極過程  (CB07040U) ,  腐食基礎理論,腐食試験  (WB03020Q)

タイトルに関連する用語 (5件)： 人工 ,  Ti ,  不動態化 ,  挙動 ,  溶存酸素