緩和法によるFRP複合材料の残留応力の研究 実験的アプローチ【JST・京大機械翻訳】

Investigations of Residual stresses in FRP composite by Relaxation techniques - An experimental approach

著者 (3件)： Kabber Suraj (Research Center, Department of Mechanical Engineering, SDM College of Engineering & Technology, Dharwad -580002 and Affiliated to Visvesvaraya Technological University, Belagavi, Karnataka, India) ,  Shivakumar Gouda P.S. (Research Center, Department of Mechanical Engineering, SDM College of Engineering & Technology, Dharwad -580002 and Affiliated to Visvesvaraya Technological University, Belagavi, Karnataka, India) ,  Umarfarooq M.A. (Research Center, Department of Mechanical Engineering, SDM College of Engineering & Technology, Dharwad -580002 and Affiliated to Visvesvaraya Technological University, Belagavi, Karnataka, India)
資料名： Materials Today: Proceedings  (Materials Today: Proceedings)
巻： 52  号： P3  ページ： 1855-1864  発行年： 2022年 
JST資料番号： W3531A  ISSN： 2214-7853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,積層複合材料における残留応力を3つの半破壊的方法:Hole Dilling,Ring Core,およびSlittingによって決定する努力を行った。一方向(UD)ガラス-エポキシ(GE)複合材料[0_4/90_4]_sを,圧力10kg/cm2,温度120°C,10分の保持時間で圧縮成形法により調製した。パルス法を用いて,3つの方法で初期残留応力を近似した。各緩和過程の有限要素(FE)シミュレーションによって,キャリブレーション係数マトリックスを得た。全3つの方法の歪はカット深さとともに増加した。リングコア法における歪は,Slitting法及び穴掘削法より高かった。さらに,リングコア法から得られた残留応力は,Slitting法が続く。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 圧力 ,  ガラス ,  *残留応力 ,  シミュレーション ,  複合材料 ,  キャリブレーション ,  圧縮成形 ,  係数 ,  深さ ,  *緩和法 ,  パルス法 ,  緩和現象 ,  建設工法 ,  穴あけ
準シソーラス用語： 有限要素 , 【Automatic Indexing@JST】

著者キーワード (4件)： 残留応力 ,  スリッティング法 ,  穴あけ工法 ,  リングコア法

分類 (3件)： 機械的性質  (YH02022L) ,  ゴム・プラスチック材料試験  (HB03000F) ,  構造力学一般  (HD01000X)

タイトルに関連する用語 (6件)： 緩和法 ,  FRP ,  複合材料 ,  残留応力 ,  研究 ,  実験