プラズマ対向材料としてメカニカルアロイングとスパークプラズマ焼結により作製した三元W-5wt%V-5wt%Ta合金の展望【JST・京大機械翻訳】

A prospect of using ternary W-5 wt%V-5 wt%Ta alloy manufactured by mechanical alloying and spark plasma sintering as plasma-facing material

著者 (6件)： Cui Hongjing (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China) ,  Liu Ning (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China) ,  Luo Laima (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China) ,  Xu Yue (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China) ,  Cheng Jigui (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China) ,  Wu Yucheng (School of Materials Science and Engineering, Hefei University of Technology, Hefei 230009, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 903  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 国際熱核実験炉におけるダイバータ部品の装甲として採用したWを確保するために,三元W合金W-5wt%V-5wt%Taをメカニカルアロイングと放電プラズマ焼結により作製した。(V,Ta)富化微細粒とW富化粒を,単相体心立方構造のW-5wt%V-5wt%Taで観察した。W-5wt%V-5wt%Taは,純Wより超微細粒径,より高い相対密度,微小硬さ,および強度を有する。強化機構を推定し,結果は,結晶粒微細化,緻密化,および固溶体が,それぞれ,主要な,二次および小さな強化役割を演ずることを示した。W-5wt%V-5wt%Taは良好な照射抵抗を有した。この良好な耐照射性は,W-5wt%V-5wt%Taの高い圧縮と引張強度と共に,超微細結晶粒との関係がある。照射の損傷を3Dレーザ走査共焦点顕微鏡によって定量的に分析した。本研究は,W-5wt%V-5wt%Taが,潜在的プラズマ対向材料として応用可能であることを示唆する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  固溶体 ,  微小硬さ ,  タングステン合金 ,  緻密化 ,  相対密度 ,  結晶粒微細化 ,  引張強さ ,  ダイバータ ,  耐放射線性 ,  三次元 ,  単相 ,  *メカニカルアロイング ,  *プラズマ対向材料 ,  *放電プラズマ焼結

著者キーワード (4件)： 金属と合金 ,  機械的性質 ,  微細構造 ,  放射線効果

分類 (2件)： 機械的性質  (WB02030U) ,  粉末製造  (WC02020M)

タイトルに関連する用語 (5件)： プラズマ対向材料 ,  メカニカルアロイング ,  スパークプラズマ焼結 ,  作製 ,  展望