ZrC-SiC界面層を有する多層ZrC-TaC被覆の多重サイクルアブレーション挙動【JST・京大機械翻訳】

Multiple cyclic ablation behaviors of multilayer ZrC-TaC coating with ZrC-SiC interface layer

著者 (4件)： Hu Dou (State Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Fiber Reinforced Light-Weight Composites, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Fu Qiangang (State Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Fiber Reinforced Light-Weight Composites, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Tong Mingde (State Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Fiber Reinforced Light-Weight Composites, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Li Xiaoxuan (State Key Laboratory of Solidification Processing, Shaanxi Key Laboratory of Fiber Reinforced Light-Weight Composites, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China)
資料名： Corrosion Science  (Corrosion Science)
巻： 200  ページ： Null  発行年： 2022年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： アブレーション抵抗被覆の多重サイクルアブレーション性能を改善するために,(ZrC-TaC)/(ZrC-SiC)多層被覆を設計し,SiC被覆C/C複合材料上に溶射により作製した。多重繰返しアブレーション試験(2.4MW/m2,60s×8)の後,多層コーティングの線形変化率は,単層ZrC-TaCコーティングと比較して75%減少した。繰返しアブレーション性能の大きな改善は,Zr-Ta-O酸化物膜の温度抵抗およびZrC-SiC界面層によって誘起された界面亀裂偏向を増加させるための低Ta/Zr比の制御と関連していた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *ジルコニウム ,  *タンタル ,  *被覆 ,  溶射 ,  酸化膜 ,  *炭化ケイ素 ,  *多重化 ,  偏向 ,  多層 ,  単一層 ,  *アブレーション ,  C/C複合材料 ,  界面亀裂
準シソーラス用語： 有限要素解析 ,  *界面層 , 【Automatic Indexing@JST】

著者キーワード (5件)： C/C複合材料 ,  多層コーティング ,  アブレーション ,  ZrC-TaC ,  有限要素解析(FEA)