1773Kでの酸化に対する炭素/炭素複合材料の長期保護のための一段階パックセメンテーションにより調製した厚いSiC-Si被覆【JST・京大機械翻訳】

A thick SiC-Si coating prepared by one-step pack cementation for long-term protection of carbon/carbon composites against oxidation at 1773 K

著者 (6件)： Zhang Bei (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Yi Maozhong (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Ning Yao (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Xie Aolin (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Zhou Zhe (College of Materials Science and Engineering, Changsha University of Science and Technology, Changsha 410114, PR China) ,  Feng Zhirong (State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, PR China)
資料名： Corrosion Science  (Corrosion Science)
巻： 200  ページ： Null  発行年： 2022年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 炭素/炭素(C/C)複合材料のための厚いSiC-Siコーティングを1段階パックセメンテーション(PC)プロセスによって調製した。コーティングの微細構造,コーティングと基板の間の界面構造,および抗酸化特性を研究した。厚さ約774μmの調製したままの被覆は緻密で微小亀裂の無い構造を有していた。酸化試験結果から,SiC-Si被覆試料の重量増加は1773Kで338hの酸化後に約8.1mg・cm-2であり,破壊はないことが分かった。異なる厚さを有する被覆の耐酸化性を調査することによって,厚さが被覆性能にプラスの影響を及ぼすことが分かった。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 回復 ,  *酸化 ,  微細構造 ,  *被覆 ,  耐酸化性 ,  *拡散浸透めっき ,  修理 ,  *炭化ケイ素 ,  微小亀裂 ,  *C/C複合材料
準シソーラス用語： 界面構造 ,  抗酸化能 ,  自己修復 ,  *パックセメンテーション , 【Automatic Indexing@JST】

著者キーワード (4件)： SiC-Si被覆 ,  長期酸化抵抗 ,  自己修復 ,  炭素/炭素複合材料

分類 (2件)： 非金属材料へのセラミック被覆  (YC02040K) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (9件)： 酸化 ,  炭素 ,  炭素複合材料 ,  長期 ,  段階 ,  パックセメンテーション ,  調製 ,  SiC ,  Si