高効率厚膜OSCのためのElectron欠損TVTユニットベースD-A高分子ドナー【JST・京大機械翻訳】

Electron-deficient TVT unit-based D-A polymer donor for high-efficiency thick-film OSCs

著者 (16件)： Zhang Liting (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Zhang Liting (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Chang Yilin (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Chang Yilin (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Zhu Xiangwei (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Yang Chen (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Yang Chen (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Shi Yanan (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Shi Yanan (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Zhang Jianqi (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Sun Xiangnan (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Sun Xiangnan (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Lu Kun (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Lu Kun (University of Chinese Academy of Sciences, Beijing, People’s Republic of China) ,  Wei Zhixiang (CAS Key Laboratory of Nanosystem and Hierarchical Fabrication, CAS Center for Excellence in Nanoscience, National Center for Nanoscience and Technology, Beijing, People’s Republic of China) ,  Wei Zhixiang (University of Chinese Academy of Sciences, Beijing, People’s Republic of China)
資料名： Nanotechnology  (Nanotechnology)
巻： 33  号： 6  ページ： 065401 (8pp)  発行年： 2022年 
JST資料番号： W0108A  ISSN： 0957-4484  CODEN： NNOTER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 有機太陽電池(OSC)の電力変換効率が近年連続的に改善されたので,OSCの工業生産と実用化に多くの注意が払われる。しかし,大規模生産プロセスにおいて解決すべき多くの問題がある。それらの中で,材料のコストを減らし,活性層の膜厚耐性を強化することは,2つのキーポイントである。したがって,高効率で厚膜のOSCの構築に適した有機半導体材料の開発が急務である。本研究では,そのユニークな共平面構造のため(E)-2-[2-(チオフェン-2-イル)ビニル]チオフェン(TVT)単位)に焦点を当てた。また,TVTは,以前の報告における電子供与ユニットとして主に使用された。しかし,フッ素原子/エステル基の導入により,TVTを電子吸引ユニットに修飾した。そして,2つの新しいドナー-アクセプタ(D-A)共重合体を,電子吸引性TVTユニットとベンゾ[2,1-b:4,5-b′]ジチオフェン(BDT)ユニットを組み合わせて得た。それらの中で,エステル修飾TVT単位に基づく高分子は,その良好な溶解性と好ましい分子積層モードにより優れた光起電力性能を示し,また,対応するデバイスは,異常に高い厚み耐性を示す。この新しい電子吸引性TVTユニットの出現は,低コスト,高効率,厚膜OSCの開発をさらに促進するであろう。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： アクセプタ ,  光起電力 ,  *ドナー ,  エステル ,  *高分子 ,  平面構造 ,  膜厚 ,  *厚膜 ,  活性層 ,  生産プロセス ,  工業生産 ,  溶解性
準シソーラス用語： *高効率 ,  有機太陽電池 ,  電力変換効率 , 【Automatic Indexing@JST】

分類 (2件)： 固体デバイス製造技術一般  (NC03030V) ,  太陽電池  (NC03084O)

タイトルに関連する用語 (7件)： 高効率 ,  厚膜 ,  欠損 ,  TVT ,  ユニットベース ,  高分子 ,  ドナー