鉱物-微粉末/メタカオリン系ジオポリマの反応速度と機械的性質【JST・京大機械翻訳】

Reaction kinetics and mechanical properties of a mineral-micropowder/metakaolin-based geopolymer

著者 (5件)： Wang Xu (School of Materials Science and Engineering, Yancheng Institute of Technology, Yancheng, Jiangsu, 224051, PR China) ,  Wang Xu (School of Materials Science and Engineering, Anhui University of Science and Technology, Huainan, Anhui, 232001, PR China) ,  Zhang Changsen (School of Materials Science and Engineering, Yancheng Institute of Technology, Yancheng, Jiangsu, 224051, PR China) ,  Zhu Huajun (School of Materials Science and Engineering, Yancheng Institute of Technology, Yancheng, Jiangsu, 224051, PR China) ,  Wu Qisheng (School of Materials Science and Engineering, Yancheng Institute of Technology, Yancheng, Jiangsu, 224051, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 10  ページ： 14173-14181  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,メタカオリンを鉱物微粉末と部分的に置換し,鉱物-微粉末/メタカオリン系ジオポリマーをアルカリ活性化下で調製し,種々のジオポリマー試料の圧縮および曲げ強度を測定した。ジオポリマ反応速度論をJohnson-Mehl-Avrami-Kolmogorovモデルを用いて調べ,メタカオリン系ジオポリマーの特性と構造に及ぼす鉱物-微粉末含有量の影響を調べた。結果は,微粉末添加がジオポリマーの機械的特性,微細構造,および反応熱に著しい影響を及ぼすことを明らかにした。30wt%の粉末含有量で,重合体は優れた機械的性質を示した。さらに,28日間硬化した試料の圧縮および曲げ強度は58.3MPaおよび12.6MPaであり,それは対照群のものよりそれぞれ24.1%および40%高かった。一方,ジオポリマー凝結時間は,鉱物微粉末中のカルシウムの存在がジオポリマー化反応を促進するので,著しく減少した。したがって,マルチゲル相の形成はジオポリマー構造をかなり強化した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *機械的性質 ,  硬化 ,  *鉱物 ,  重合体 ,  *反応速度 ,  微細構造 ,  *粉体 ,  カルシウム ,  *カオリン ,  活性化 ,  反応熱 ,  *微粉体 ,  反応速度論
準シソーラス用語： *メタカオリン ,  *ジオポリマ ,  凝結時間 , 【Automatic Indexing@JST】

著者キーワード (4件)： ジオポリマ ,  鉱物微粉末 ,  反応速度論 ,  機械的性質

分類 (3件)： セメントの性質・分析  (YC05040F) ,  セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (6件)： 鉱物 ,  微粉末 ,  メタカオリン ,  ジオポリマ ,  反応速度 ,  機械的性質