天然資源からの炭素発泡体に及ぼす強化材としての黒鉛負荷の影響【JST・京大機械翻訳】

The Effect of Graphite Loading as Reinforcement on Carbon Foam from Natural Resources

著者 (4件)： Hassan Nur Zaha (Universiti Tun Hussein Onn Malaysia, Nano Structure and Surface Modification Research Group, Faculty of Mechanical and Manufacturing Engineering Malaysia) ,  Mohamed Hatta Mohamed Nasrul (Universiti Tun Hussein Onn Malaysia, Nano Structure and Surface Modification Research Group, Faculty of Mechanical and Manufacturing Engineering Malaysia) ,  Badarulzaman Nur Azam (Universiti Tun Hussein Onn Malaysia, Nano Structure and Surface Modification Research Group, Faculty of Mechanical and Manufacturing Engineering Malaysia) ,  Mohd Joharudin Nurul Farahin (Universiti Tun Hussein Onn Malaysia (UTHM), Faculty of Mechanical and Manufacturing Engineering Parit Raja Malaysia Johor)
資料名： Key Engineering Materials  (Key Engineering Materials)
巻： 908  ページ： 9-13  発行年： 2022年 
JST資料番号： D0744C  ISSN： 1013-9826  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 本研究は,機械的及び物理的特性に及ぼす天然資源炭素発泡体に及ぼす強化材料としてのグラファイトの影響を決定することである。スクロースを炭素前駆体として用い,0wt%~0.3wt%の種々の濃度のグラファイトを炭素フォームに添加した。カーボンフォームを鋳型法を用いて調製し,続いて予備硬化と炭化プロセスを行った。予備硬化プロセスは250°Cで行われ,炭化プロセスは不活性雰囲気下で900°Cで行った。形態,多孔性,密度および圧縮強度を,この実験で特徴づけた。走査Electron顕微鏡(SEM)を通して,グラファイトは,明らかに,「窓に埋め込まれ,ボイド空間を満たすことができる。黒鉛濃度が増加したとき,炭素フォームの空隙率は減少し,グラファイト濃度が増加したとき,炭素フォームの密度が増加した。0.3wt%グラファイトを添加した炭素発泡体は,グラファイト無添加のカーボンフォーム(0.95N/mm2)と比較して,最高の圧縮強度(1.84N/mm2)を示した。炭素フォームの特性はグラファイト負荷の添加によって著しく影響される。Copyright 2022 Trans Tech Publications Ltd. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  密度 ,  *炭素 ,  *グラファイト ,  多孔性 ,  炭化 ,  *補強材料 ,  形態 ,  圧縮強さ ,  前駆体 ,  空隙率 ,  *多孔質体
準シソーラス用語： 天然資源 ,  *炭素発泡体 , 【Automatic Indexing@JST】

著者キーワード (5件)： グラファイト ,  スクロース ,  カーボンフォーム ,  天然資源 ,  機械的性質

分類 (3件)： 機械的性質  (YH02022L) ,  セラミック・陶磁器の製造  (YC03020V) ,  発泡成形  (YH04070U)

タイトルに関連する用語 (4件)： 天然資源 ,  炭素発泡体 ,  強化材 ,  黒鉛