第一原理計算に基づく単結晶ニッケルの予測結晶塑性モデリング【JST・京大機械翻訳】

Predictive Crystal Plasticity Modeling of Single Crystal Nickel Based on First-Principles Calculations

著者 (6件)： Shimanek John D. (Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA, USA) ,  Qin Shipin (Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA, USA) ,  Shang Shun-Li (Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA, USA) ,  Liu Zi-Kui (Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA, USA) ,  Beese Allison M. (Department of Materials Science and Engineering, The Pennsylvania State University, University Park, PA, USA) ,  Beese Allison M. (Department of Mechanical Engineering, The Pennsylvania State University, University Park, PA, USA)
資料名： JOM  (JOM)
巻： 74  号： 4  ページ： 1423-1434  発行年： 2022年 
JST資料番号： C0321A  ISSN： 1047-4838  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 結晶塑性有限要素法内の実験フィッティングデータへの依存性を低減するために,密度汎関数理論(DFT)に基づく第一原理計算を統合し,純Ni単結晶の歪硬化挙動を予測した。流動抵抗を,第一原理計算におけるスーパーセルに歪を課すことによってモデル化した硬化挙動によって,DFTベースの方法によって計算した理想せん断強度と弾性特性を用いてPeierls-Nabarro方程式を通して評価した。単独では,純刃状転位の弾性相互作用が,単一すべり系の小さな歪に対する硬化挙動を捕捉する。より大きな歪に対して,硬化は,端部とスクリューの流動抵抗成分の歪加重線形結合を通して捉えられる。組合せの速度は本フレームワークでは予測されないが,多重負荷方向に対する大きな歪(ΔΔ0.4)による実験との一致は,メソスケール物理の解析モデルの組み込みを通して,より予測的な結晶塑性モデリングのための可能な経路を示す。Copyright The Minerals, Metals & Materials Society 2022 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *塑性 ,  *単結晶 ,  有限要素法 ,  *ニッケル ,  剪断強さ ,  刃状転位 ,  *モデリング ,  多重化 ,  数学的変換 ,  密度汎関数法 ,  解析モデル
準シソーラス用語： 線形結合 ,  *第一原理計算 ,  *結晶塑性 ,  弾性特性 ,  弾性相互作用 ,  すべり系 , 【Automatic Indexing@JST】

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (6件)： 第一原理計算 ,  単結晶 ,  ニッケル ,  予測 ,  結晶塑性 ,  モデリング