部分再結晶構造から完全再結晶不均一構造へのCrCoNi中エントロピー合金の強化機構【JST・京大機械翻訳】

Strengthening mechanism of CrCoNi medium-entropy alloy from the partially recrystallized structure to the fully recrystallized heterogeneous structure

著者 (22件)： Liu Yu (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Liu Yu (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Lai Ruilin (Powder Metallurgy Research Institute, Central South University, Changsha 410083, PR China) ,  He Cunxiao (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  He Cunxiao (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Li Kai (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Li Kai (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Yang Yong (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Yang Yong (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Wu Wenke (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Wu Wenke (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Fu Zhiqiang (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Fu Zhiqiang (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Xu Shuanghui (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Xu Shuanghui (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  He Guoai (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  He Guoai (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  He Guoai (Hunan InnoChina Advanced Materials Co., Ltd, Yueyang 414000, PR China) ,  Gan Bin (Beijing Key Laboratory of Advanced High Temperature Materials, Central Iron and Steel Research Institute, Beijing 100081, PR China) ,  Huang Cheng (Light Alloy Research Institute, Central South University, Changsha 410083, PR China) ,  Huang Cheng (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, PR China) ,  Huang Cheng (Hunan InnoChina Advanced Materials Co., Ltd, Yueyang 414000, PR China)
資料名： Materials Characterization  (Materials Characterization)
巻： 186  ページ： Null  発行年： 2022年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 単相面心立方CrCoNi媒体-エントロピー合金に対する強化方法のVast量を近年実施した。本研究では,部分的に再結晶化した構造だけでなく,完全に再結晶化した不均一構造を,CrCoNi媒体-エントロピー合金に,冷間圧延とそれに続く傾斜温度下で展開する焼鈍により導入した。焼鈍試験片を引張試験し,機械的性質の詳細なパラメータを導いた。結晶粒界,転位,固溶体からの強化を定量化し,他の強化機構の存在を示唆した。広範囲なせん断帯,ナノ結晶粒,ナノ双晶,HCPラメラの外観に対する強度の増加を属性した。さらに,二重不均一構造は,アニールした試料間の同様な極限引張強度に寄与すると考えられる。さらに重要なことに,転位,積層欠陥,双晶が変形モードとしてこの合金に現れ,異常な破壊伸びに寄与する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *エントロピー ,  結晶粒界 ,  *合金 ,  固溶体 ,  *再結晶 ,  焼なまし ,  双晶 ,  転位【結晶】 ,  冷間圧延 ,  剪断帯 ,  媒質 ,  引張強さ ,  単相 ,  ナノ結晶
準シソーラス用語： ナノ双晶 , 【Automatic Indexing@JST】

著者キーワード (4件)： CrCoNi中エントロピー合金 ,  粒度の不均一性 ,  強化計算 ,  完全再結晶構造

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 再結晶 ,  不均一 ,  エントロピー ,  合金 ,  強化