cw CO_2レーザを用いたレーザ蒸発により得たt-ZrO_2:Eu3+ナノ蛍光体の研究【JST・京大機械翻訳】

Study of t-ZrO₂ : Eu³⁺ nanophosphor obtained by laser vaporisation using a cw CO₂ laser

著者 (7件)： Kostyukov A I (Novosibirsk State University) ,  Kostyukov A I (Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, Novosibirsk, Russian Federation) ,  Nashivochnikov A A (Novosibirsk State University) ,  Nashivochnikov A A (Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, Novosibirsk, Russian Federation) ,  Snytnikov V N (Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, Novosibirsk, Russian Federation) ,  Rakhmanova M I (Nikolaev Institute of Inorganic Chemistry, Siberian Branch of the Russian Academy of Sciences, Novosibirsk, Russian Federation) ,  Snytnikov V N (Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences, Novosibirsk, Russian Federation)
資料名： Quantum Electronics  (Quantum Electronics)
巻： 52  号： 2  ページ： 149-154  発行年： 2022年 
JST資料番号： D0044C  ISSN： 1063-7818  CODEN： QUELEZ  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ZrO_2:Eu3+ナノ蛍光体をCO_2レーザを用いて特定組成のセラミックターゲットの蒸発により作製し,続いてアルゴン流中で蒸気凝縮した。球形形態を有するナノ粒子を0.1atmの圧力で合成した。t-ZrO_2相は支配的(98%)であることが分かった。透過型電子顕微鏡データによると,ナノ粒子サイズは10±4nmであった。作製したナノ粒子のルミネセンス特性を研究した。試料の強い赤色ルミネセンスは主に591と606nmのバンドピークに起因し,これはt-ZrO_2構造中のEu3+イオンの5D_0→7F_1と5D_0→7F_2遷移にそれぞれ関係している。また,ユウロピウムはレーザ合成時にZrO_2マトリックス上に均一に分布していることを示した。t-ZrO_2:Eu3+ナノ蛍光体と初期粗粒ターゲットの比較研究を行った。レーザ蒸発の提案した方法が,t-ZrO_2系ナノ蛍光体の合成に有望であると結論した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 凝縮 ,  *蒸発 ,  セラミック ,  ターゲット ,  ルミネセンス ,  アルゴン ,  *ユウロピウム ,  透過型電子顕微鏡 ,  ナノ粒子
準シソーラス用語： 粗粒子 ,  *ナノ蛍光体 , 【Automatic Indexing@JST】

分類 (2件)： 固体レーザ  (BD04080W) ,  無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (5件)： CW ,  レーザ ,  蒸発 ,  ナノ蛍光体 ,  研究