超安定リチウムおよびナトリウムイオン電池のための階層的SnO_2@NC@MoS_2/Cナノチューブの構築【JST・京大機械翻訳】

Construction of Hierarchical SnO₂@NC@MoS₂/C Nanotubes for Ultrastable Lithium- and Sodium-Ion Batteries

著者 (24件)： Ye Bingqing (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Xu Lei (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Wu Wenbo (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Ye Yuliang (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Yang Zunxian (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Yang Zunxian (Fujian Science & Technology Innovation Laboratory For Optoelectronic Information of China, Mindu Innovation Laboratory, P. R. China) ,  Qiu Yinglin (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Gong Zhipeng (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Zhou Yuanqing (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Huang Qiaocan (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Shen Zihong (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Hong Zeqian (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Meng Zongyi (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Zeng Zhiwei (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Cheng Zhiming (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Ye Songwei (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Hong Hongyi (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Lan Qianting (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Li Fushan (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Li Fushan (Fujian Science & Technology Innovation Laboratory For Optoelectronic Information of China, Mindu Innovation Laboratory, P. R. China) ,  Guo Tailiang (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Guo Tailiang (Fujian Science & Technology Innovation Laboratory For Optoelectronic Information of China, Mindu Innovation Laboratory, P. R. China) ,  Xu Sheng (National & Local United Engineering Laboratory of Flat Panel Display Technology, Fuzhou University, P. R. China) ,  Xu Sheng (Fujian Science & Technology Innovation Laboratory For Optoelectronic Information of China, Mindu Innovation Laboratory, P. R. China)
資料名： ACS Sustainable Chemistry & Engineering  (ACS Sustainable Chemistry & Engineering)
巻： 10  号： 10  ページ： 3166-3179  発行年： 2022年 
JST資料番号： W5047A  ISSN： 2168-0485  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本研究では,新しい階層的管状構造(SnO_2@NC@MoS_2/C)を設計し,中空管のための犠牲テンプレートとしてMnO_xナノワイヤを用いて合成し,SnO_2層,窒素ドープ炭素(NC)層,および炭素層中に取り込んだ超薄MoS_2ナノシートを連続して包んだ。このような特定の構造において,SnO_2とMoS_2の伝導率は明らかに改善され,リチウム/ナトリウムイオン(Li+/Na+)インターカレーション/脱インターカレーションによる大きな体積変化も効果的に緩和された。特に,グルコースに由来する最外部炭素に起因するMoS_2層間の間隔の拡大により,層間のLi+/Na+のシャットリングが容易になる。上記の利点により,階層的中空ナノ構造は,異なる成分の相乗効果を特徴とし,SnO_2@NC@MoS_2/Cナノ複合材料は,リチウムイオン電池に適用した場合,例外的な放電容量(0.2Ag-1で980.9mAhg-1)と長いサイクル安定性(450サイクルで750mAhg-1)を示した。2,5および10Ag-1でさえ,比容量は500サイクル後にそれぞれ672.7,630.1および565mAh g-1に達し,これは超安定高速サイクル性能を示した。一方,ナトリウムイオン電池に用いる複合材料を用いた場合,優れた容量(150サイクル以上0.2Ag-1で479.3mAhg-1),小さな容量減衰速度(1Ag-1で2000サイクル後のサイクル当たり0.06%),および優れたレート容量(それぞれ0.1,0.2,0.5,2,および5Ag-1で818.5,691.6,577.6,506.3,442.4,および348.2mAhg-1)を達成した。Copyright 2022 American Chemical Society All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 性能 ,  相乗作用 ,  鋳型反応 ,  静電容量 ,  ナノ構造 ,  *インターカレーション ,  電池容量 ,  リチウムイオン電池 ,  ナノワイヤ ,  ナノシート ,  ヘキソース ,  アルドース
準シソーラス用語： 放電容量 ,  二層 ,  窒素ドーピング ,  *ナトリウムイオン蓄電池 ,  比容量 ,  サイクル性能 ,  伝導率 ,  犠牲テンプレート , 【Automatic Indexing@JST】

著者キーワード (6件)： 階層的管状構造 ,  極薄ナノシート ,  拡張層間間隔 ,  相乗効果 ,  リチウムイオン電池 ,  ナトリウムイオン電池

分類 (1件)： 二次電池  (YB04030K)

物質索引 (1件)： グルコース

タイトルに関連する用語 (4件)： リチウム ,  ナトリウムイオン電池 ,  ナノチューブ ,  構築