異なる温度での圧延によるAl-Cu-Li合金の機械的性質強化とミクロ組織変化【JST・京大機械翻訳】

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

著者 (7件)： Wang Lin (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, China) ,  Wang Lin (College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China) ,  Wang Lin (Light Alloys Research Institute, Central South University, Changsha 410083, China) ,  Kong Charlie (Mark Wainwright Analytical Centre, University of New South Wales, Sydney, NSW 2052, Australia) ,  Yu Hailiang (State Key Laboratory of High Performance Complex Manufacturing, Central South University, Changsha 410083, China) ,  Yu Hailiang (College of Mechanical and Electrical Engineering, Central South University, Changsha 410083, China) ,  Yu Hailiang (Light Alloys Research Institute, Central South University, Changsha 410083, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 900  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Al-Cu-Li合金をモデル材料として選択し,極低温における変形強化の機構への洞察を得た。対称圧延と非対称圧延(圧延比1.3)で作製した合金の機械的性質とミクロ組織の変化を種々の温度(25°C,-100°C,-190°C)で調べた。より小さな結晶粒と緻密な転位が低温圧延試料で観察され,室温で加工した試料と比較して強度増強をもたらした。不均一結晶粒組織は,-100°Cで低温圧延(CR)によって処理した試料の粗くて微細な結晶粒から作られ,それは,-190°Cと室温圧延でCRによって加工されたものより,より高い強度とより良い延性をもたらした。最後に,新しいバック応力モデルを採用して,不均一構造の降伏強さを計算し,100°CでCRによって処理した試料の最高強度を説明した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  *機械的性質 ,  *合金 ,  対称性 ,  低温 ,  *リチウム合金 ,  *金属組織 ,  *圧延 ,  非対称性 ,  結晶粒 ,  極低温 ,  降伏強さ ,  異周速圧延
準シソーラス用語： 結晶粒組織 , 【Automatic Indexing@JST】

著者キーワード (4件)： Al-Cu-Li合金 ,  非対称冷凍圧延 ,  機械的性質 ,  微細構造