プラズマ溶射により作製したマイクロナノFeCoNiCrMnAl_0.5被覆の微細構造と腐食特性【JST・京大機械翻訳】

Microstructure and corrosion properties of micro-nano FeCoNiCrMnAl_0.5 coatings fabricated by plasma spraying

著者 (12件)： Mao Xingye (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Mao Xingye (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China) ,  Wang Yuxin (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Wang Yuxin (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China) ,  Jiang Jie (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Jiang Jie (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China) ,  Chi Yunlong (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Chi Yunlong (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China) ,  Dong Yanchun (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Dong Yanchun (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China) ,  Yang Yong (Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology, School of Materials Science and Engineering, State Key Laboratory of Reliability and Intelligence of Electrical Equipment, Hebei University of Technology, 300132 Tianjin, China) ,  Yang Yong (School of Materials Science and Engineering, Hebei University of Technology, Tianjin 300132, China)
資料名： Materials Letters  (Materials Letters)
巻： 314  ページ： Null  発行年： 2022年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,FeCoCrNiMnAl_0.5高エントロピー合金被覆を,メカニカルアロイングにより自家製のFeCoCrNiMnAl_0.5粉末をプラズマ溶射してQ235鋼の表面上に作製した。3.5wt%NaCl溶液中のFeCoCrNiMnAl_0.5HEA被覆の電位-動的分極曲線を電気化学ワークステーションを用いて試験した。HEA被覆の相は,溶射中に体心立方から面心立方に変態する。被覆の腐食電位は316ステンレス鋼と304ステンレス鋼のそれより高く,HEA被覆は9.56×10-6A/cm2の腐食電流密度を持ち,それは316ステンレス鋼(1.16×10-5A/cm2)のそれより低く,304ステンレス鋼(7.35×10-6A/cm2)のものよりわずかに高かった。被覆の腐食速度は316ステンレス鋼の1/2であった。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 電位 ,  *腐食 ,  粉体 ,  ステンレス鋼 ,  炭素鋼 ,  *被覆 ,  腐食速度 ,  *プラズマ溶射 ,  *溶射 ,  塩化ナトリウム ,  腐食電流 ,  腐食電位 ,  メカニカルアロイング
準シソーラス用語： 分極曲線 ,  Q235鋼 ,  SUS304 , 【Automatic Indexing@JST】

著者キーワード (6件)： メカニカルアロイング ,  プラズマ溶射 ,  FeCoCrNiMnAl_0.5 ,  微細構造 ,  腐食 ,  高エントロピー合金

分類 (1件)： 溶射  (WC08030N)

タイトルに関連する用語 (4件)： プラズマ溶射 ,  作製 ,  微細構造 ,  腐食特性