プラズマ溶射Cr_2O_3-TiO_2被覆のトライボロジー挙動に及ぼすグラファイト添加の影響【JST・京大機械翻訳】

Effect of graphite addition on tribological behaviour of plasma sprayed Cr₂O₃-TiO₂ coating

著者 (4件)： Bagde Pranay (Department of Mechanical Engineering, Government College of Engineering (GCOE), Chandrapur 442403, India) ,  Mehar Sanket (Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, India) ,  Sapate SG (Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, India) ,  Rathod Avishkar (Department of Metallurgical and Materials Engineering, Visvesvaraya National Institute of Technology (VNIT), South Ambazari Road, Nagpur 440010, India)
資料名： Materials Today: Proceedings  (Materials Today: Proceedings)
巻： 56  号： P4  ページ： 2365-2370  発行年： 2022年 
JST資料番号： W3531A  ISSN： 2214-7853  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Cr_2O_3-TiO_2+Niグラファイトセラミック被覆をプラズマ溶射法を用いて堆積した。被覆のトライボロジー挙動を決定するためにアブレシブ摩耗試験を行った。摩耗と摩擦試験を,異なる荷重と固定滑り速度で行った。堆積と摩耗した被覆の構造的および機械的特性化を行った。X線光電子分光(XPS)も用いて種々の酸化物の形成を確認した。結果は,Cr_2O_3-TiO_2被覆におけるグラファイト添加によって,摩擦係数が18~44%減少し,摩耗率が1.3~2倍減少することを示した。破壊靭性の改善も得られ,Cr_2O_3-TiO_2-Niグラファイトコーティングの良好な耐摩耗性につながった。また,トライボ膜形成と責任摩耗メカニズムのシーケンスを指摘した。本研究の結果は,被覆のトライボロジー挙動に及ぼす熱処理と被覆厚さの影響を研究する方法を導くことができる。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 耐摩耗性 ,  摩擦係数 ,  摩耗 ,  *被覆 ,  *プラズマ溶射 ,  破壊靱性 ,  *グラファイト ,  摩擦試験 ,  セラミック被覆 ,  滑り速度 ,  アブレシブ摩耗 ,  摩耗率
準シソーラス用語： *トライボロジー挙動 ,  摩耗機構 ,  トライボ膜 , 【Automatic Indexing@JST】

著者キーワード (5件)： コーティング ,  Cr_2O_3 ,  摩擦 ,  グラファイト ,  トライボフィルム

分類 (2件)： 潤滑一般  (QB02010S) ,  溶射  (WC08030N)

タイトルに関連する用語 (3件)： プラズマ溶射 ,  トライボロジー挙動 ,  グラファイト