バクテリアセルロース/コラーゲン/ポリビニルアルコールナノファイバーヒドロゲル膜の機械的及び熱的性質強化及び膨潤挙動【JST・京大機械翻訳】

Mechanical and Thermal Properties Enhancement and Swelling Behavior of Bacterial Cellulose/Collagen/Polyvinyl Alcohol Nanofiber Hydrogel Film

著者 (6件)： Yang Qun (School of Textiles and Fashion, Shanghai University of Engineering Science, Shanghai, China) ,  Yang Qun (Shanghai Engineering Research Center for Clean Production of Textile Chemistry, Shanghai, China) ,  Yang Qun (Key Laboratory of Yarn Materials Forming and Composite Processing Technology, Zhejiang, China) ,  Wang Jinfeng (Institute for Frontier Materials, Deakin University, Geelong, VIC, Australia) ,  Yao Yongbo (Key Laboratory of Yarn Materials Forming and Composite Processing Technology, Zhejiang, China) ,  Dai Zhengwei (Key Laboratory of Yarn Materials Forming and Composite Processing Technology, Zhejiang, China)
資料名： Fibers and Polymers  (Fibers and Polymers)
巻： 23  号： 2  ページ： 305-314  発行年： 2022年 
JST資料番号： W4363A  ISSN： 1229-9197  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 細菌セルロース/コラーゲン/ポリビニルアルコールの複合ヒドロゲル膜を,細菌セルロースヒドロゲル(BC)をベース材料として用い,コラーゲン(COL)とポリビニルアルコール(PVA)を強化材料として導入し,特に破断時の引張強度を向上した。複合ヒドロゲル膜の形態,機械的性質および熱安定性も調べた。膨潤挙動を,Schottの二次膨潤モデルを用いて詳細に研究した。研究結果は,BC/PVA/COL複合材料が,BCの破断点伸びの181.9%の改善を示した。さらに,架橋処理後,得られたBC/PVA/COL複合膜の引張強度は12.9%向上した。重要なことに,更なる研究は,複合ヒドロゲルフィルムの構造安定性と熱安定性が著しく強化されたことを示した。DI水中のBCと複合ナノファイバーヒドロゲル膜の膨潤挙動は,Schottの二次膨潤モデルに従い,複合材料の膨潤は架橋処理後に著しく減少した。Copyright The Korean Fiber Society for Fibers and Polymers and Springer 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  複合材料 ,  *膨潤 ,  破断 ,  *ポリビニルアルコール ,  熱安定性 ,  架橋【高分子】 ,  *コラーゲン ,  補強材料 ,  引張強さ ,  *熱特性 ,  複合膜 ,  *ヒドロゲル
準シソーラス用語： *バクテリアセルロース ,  破断伸度 , 【Automatic Indexing@JST】

著者キーワード (5件)： 細菌セルロース ,  ヒドロゲルフィルム ,  ポリビニルアルコール ,  膨潤挙動 ,  Schottの二次膨潤モデル

分類 (2件)： 多糖類  (CF10054P) ,  その他の高分子材料  (YH07150C)

タイトルに関連する用語 (6件)： バクテリアセルロース ,  コラーゲン ,  熱的性質 ,  強化 ,  膨潤 ,  挙動