誘導歯槽骨再生のための3DプリントTi-Nb合金メッシュ上への新規半透性コーティングの電気泳動析出【JST・京大機械翻訳】

Electrophoretic deposition of novel semi-permeable coatings on 3D-printed Ti-Nb alloy meshes for guided alveolar bone regeneration

著者 (25件)： Zhao Danlei (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Zhao Danlei (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Zhao Danlei (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Zhao Danlei (State Key Lab of Materials Processing and Die & Mould Technology, School of Materials, Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China) ,  Dong Haoran (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Dong Haoran (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Dong Haoran (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Niu Yuting (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Niu Yuting (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Niu Yuting (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Fan Wenjie (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Fan Wenjie (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Fan Wenjie (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Jiang Muqi (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Jiang Muqi (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Jiang Muqi (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Li Ke (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Li Ke (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Li Ke (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Wei Qingsong (State Key Lab of Materials Processing and Die & Mould Technology, School of Materials, Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China) ,  Palin William M. (Dental and Biomaterials Sciences, School of Dentistry, Institute of Clinical Sciences, College of Medical and Dental Sciences, University of Birmingham, UK) ,  Zhang Zhen (Department of Stomatology, Union Hospital, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430022, China) ,  Zhang Zhen (School of Stomatology, Tongji Medical College, Huazhong University of Science and Technology, Wuhan 430030, China) ,  Zhang Zhen (Hubei Province Key Laboratory of Oral and Maxillofacial Development and Regeneration, Wuhan 430022, China) ,  Zhang Zhen (Dental and Biomaterials Sciences, School of Dentistry, Institute of Clinical Sciences, College of Medical and Dental Sciences, University of Birmingham, UK)
資料名： Dental Materials  (Dental Materials)
巻： 38  号： 2  ページ： 431-443  発行年： 2022年 
JST資料番号： D0009C  ISSN： 0109-5641  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ガイドされた骨再生(GBR)技術は,骨欠損の部位特異的増殖のために,肺胞リッジを増強するためにバリア膜を使用する。しかし,鋳造金属下部構造を用いた現在のアプローチは,手術部位への不十分な適応と感染のリスク増加を示す。本研究は,3D印刷多孔性チタン-ニオブ(Ti-Nb)合金メッシュを空間を維持し,線維芽細胞の成長を防ぎ,GBRに対する細菌のコロニー形成を阻害する多機能被覆を作製することを目的とした。Ti-Nb合金メッシュを選択的レーザ融解(SLM)によって調製し,新しい表面被覆用基板として使用した。多孔性キトサン(CS)/ゼラチン(G)/ドキシサイクリン(Dox)被覆を電気泳動析出(EPD)と凍結乾燥を用いてメッシュ上に形成した。EPDのプロセスを,Fourier変換赤外分光法(FT-IR),ゼータ電位,および粒径分析によって特性評価した。コーティングの細胞毒性を骨芽細胞と免疫染色の培養によって評価した。Staphylococcus aureus(黄色ぶどう球菌)および走査電子顕微鏡(SEM)に対する阻害ゾーン試験を用いて,被覆の抗菌活性を試験した。線維芽細胞浸潤と栄養移動特性の阻害は,免疫染色と透過性試験を用いて分析した。Ti-Nb合金バルク試料において,高い降伏強度(567.5±3.5MPa)と低い弾性係数(65.5±0.2GPa)を達成した。ゼータ電位,FT-IRおよびSEMのデータは,多孔性スポンジコーティングがEPD後に化学的に結合されることを示した。CSGDox1(1mg・mL-1のDoxを含む)のin vitro分析は,その抗菌効果と生体適合性を明らかにした。さらに,CSGDox1被覆は,線維芽細胞の増殖を防ぐのに有効であり,一方,栄養素の浸潤を可能にした。本研究は,3DプリントTi-Nbメッシュ上のCSGDox被覆のEPDが,空間を維持し,抗生物質放出を提供し,一方,GBR治療の成功に必須である軟組織成長に対する障壁を維持することを示した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  *被覆 ,  浸潤 ,  ζ電位 ,  ゼラチン ,  抗生物質 ,  *骨形成 ,  線維芽細胞 ,  キトサン ,  *三次元 ,  軟部組織 ,  生体適合性 ,  骨芽細胞 ,  免疫染色 ,  *電気泳動堆積
準シソーラス用語： *骨再生 , 【Automatic Indexing@JST】

著者キーワード (6件)： 誘導骨再生 ,  3D印刷 ,  電気泳動析出 ,  キトサン ,  ゼラチン ,  ドキシサイクリン

分類 (1件)： 医用素材  (GA05040H)

タイトルに関連する用語 (8件)： 誘導 ,  歯槽骨再生 ,  3D ,  Ti ,  Nb合金 ,  メッシュ ,  コーティング ,  電気泳動析出