単結晶超合金のレーザ指向凝固中の迷粒形成を阻害する新しい戦略【JST・京大機械翻訳】

A new strategy to inhibit stray grain formation during laser directed solidification of single crystal superalloys

著者 (20件)： Wang Jiawei (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Wang Jiawei (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Wang Huaming (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Wang Huaming (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Wang Huaming (Research Institute for Frontier Science, Beihang University, 37 Xueyuan Road, Beijing, China) ,  Li Kangjie (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Li Kangjie (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Chen Mingyuan (School of Aeronautic Science and Engineering, Beihang University, Beijing 100191, China) ,  Zhang Meiling (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Zhang Meiling (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Zhang Bo (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Zhang Bo (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Yuan Jingwei (School of Materials Science and Engineering, Beihang University, Beijing 100191, China) ,  Yuan Jingwei (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Cheng Xu (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Cheng Xu (Research Institute for Frontier Science, Beihang University, 37 Xueyuan Road, Beijing, China) ,  Zhang Shuquan (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Zhang Shuquan (Research Institute for Frontier Science, Beihang University, 37 Xueyuan Road, Beijing, China) ,  Wang Yudai (National Engineering Laboratory of Additive Manufacturing for Large Metallic Components, Beijing 100191, China) ,  Wang Yudai (Research Institute for Frontier Science, Beihang University, 37 Xueyuan Road, Beijing, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 906  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： レーザ表面再融解はニッケル基単結晶(SX)超合金部品を修復する優れた可能性を示すが,粒子構造を制御し,一方,浮遊粒子(SG)形成を避けることは産業においてまだ課題である。ニッケル超合金のSG形成を抑制するために,本論文では,新しい回転レーザ照射法を導入し,レーザ指向凝固プロセスにおけるSG生成の起源を研究した。さらに,溶融池の底部でのSG形成のメカニズムを明らかにするために,エピタキシャル成長処理中の等軸結晶粒形成の傾向を有する複合合金組成の数値モデルを開発した。その結果,溶融池の底部に形成されたSGは,主に粗い溶融界面を有する等軸粒変態の著しく増大した可能性に起因することを示した。レーザプロセスの間,SGの数は,レーザ照射と重力方向の間の角度(θ)の増加で徐々に減少する。θ=90°では,滑らかな融合界面を有するプールにおいて,SGのない[001]デンドライトの良く配向したエピタキシャル成長が観察された。さらに,レーザ方向性凝固中のこの現象に基づく新しいレーザ蒸着技術の適用は,単結晶成分のための工業的製造における結晶粒配向成長を制御する有効な方法である。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： エピタクシー ,  界面 ,  重力 ,  *単結晶 ,  融解 ,  ニッケル ,  *超合金 ,  樹枝状結晶 ,  レーザ照射 ,  結晶粒 ,  溶融池 ,  配向 ,  レーザ蒸着
準シソーラス用語： 再融解 ,  *方向性凝固 , 【Automatic Indexing@JST】

著者キーワード (4件)： ニッケル基単結晶超合金 ,  迷走 ,  柱状から平衡への転移 ,  レーザ表面融解

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  肉盛  (WC07060N)

タイトルに関連する用語 (5件)： 単結晶超合金 ,  レーザ ,  指向凝固 ,  阻害 ,  戦略