インジウムドープコバルトフリー60wt%Ce_0.9Pr_0.1O_2-δ-40wt.%Pr_0.6Sr_0.4Fe_1-xIn_xO_3-δ酸素輸送膜の高CO_2抵抗【JST・京大機械翻訳】

High CO₂ resistance of indium-doped cobalt-free 60 wt.%Ce_0.9Pr_0.1O_2-δ-40 wt.%Pr_0.6Sr_0.4Fe_1-x In _x O_3-δ oxygen transport membranes

著者 (8件)： Huang Yanhao (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Zhang Chao (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Wang Xiaopeng (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Li Dongcheng (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Zeng Lingyong (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  He Yiyi (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Yu Peifeng (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...) ,  Luo Huixia (School of Materials Science and Engineering, State Key Laboratory of Optoelectronic Materials and Technologies, Key Lab of Polymer Composite & Functional Materials, Guangzhou Key Laboratory of Flexible Electronic Materials and Wearable Devices, Sun Yat-Sen University, No. 135, Xingang Xi ...)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 1  ページ： 415-426  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 酸素輸送膜(OTM)は,酸素富化燃焼に基づくガス分離と炭素中和における巨大な応用展望を有する。この論文では,インジウムをドープした60wt%Ce_0.9Pr_0.1O_2-δ-40wt%Pr_0.6Sr_0.4Fe_1-xIn_xO_3-δ(CPO-PSF_1-xI_xO,x=0.01,0.025,0.075,0.1)コバルトフリー二相MIEC OTMsをPechini法により成功裏に調製した。これらのOTMの相構造,表面形態,元素分布,酸素透過性,および長期操作安定性を系統的に調査した。これらのOTMの中で,CPO-PSF_0.99I_0.01Oのチャンピオン酸素透過性フラックスは,空気/He勾配および空気/CO_2勾配下で,1000°Cで1.07mL・min-1・cm-2および0.80mL・min-1・cm-2に達した。一方,CPO-PSF_0.99I_0.01Oは,純粋CO_2を掃引ガスとして1000°Cで100時間着実に0.80mL・min-1・cm-2の値を維持した。長期酸素透過性反応後のOTMの表面元素分布と相構造をXRD,EDSと組み合わせたSEMにより調べ,使用済み膜が新鮮な膜と同じ構造と成分を保持し,InドープOTMが優れたCO_2耐性を持つことを示した。これらのOTMの鉄に対する適切なインジウム置換は酸素透過性を改善するだけでなく,材料の長期反応安定性を維持する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *インジウム ,  炭素 ,  鉄 ,  ヘリウム ,  X線回折分析 ,  *ドーピング ,  中性化 ,  ガス分離
準シソーラス用語： *酸素輸送 ,  表面形態 ,  酸素透過性 ,  Pechini法 ,  酸素富化 ,  元素分布 ,  相構造 , 【Automatic Indexing@JST】

著者キーワード (5件)： 二相膜 ,  インジウム置換 ,  酸素輸送膜 ,  ガス分離 ,  CO_2耐性

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (1件)： 酸素輸送