スパークプラズマ焼結チタニア-シリコンオキシカーバイド(TiO_2/SiOC)ナノ複合材料の機械的特性評価【JST・京大機械翻訳】

Mechanical characterization of spark plasma sintered titania-silicon oxycarbide (TiO₂/SiOC) nanocomposites

著者 (4件)： Awin E.W. (Laboratory for High Performance Ceramics, Department of Metallurgic and Materials Engineering, Indian Institute of Technology-Madras (IIT Madras), Chennai, 600036, India) ,  Kumar K.C.H. (Laboratory for High Performance Ceramics, Department of Metallurgic and Materials Engineering, Indian Institute of Technology-Madras (IIT Madras), Chennai, 600036, India) ,  Bernard S. (Universite de Limoges, CNRS, IRCER, UMR 7315, F-87000, Limoges, France) ,  Kumar R. (Laboratory for High Performance Ceramics, Department of Metallurgic and Materials Engineering, Indian Institute of Technology-Madras (IIT Madras), Chennai, 600036, India)
資料名： Materialwissenschaft und Werkstofftechnik  (Materialwissenschaft und Werkstofftechnik)
巻： 53  号： 2  ページ： 235-243  発行年： 2022年 
JST資料番号： C0781A  ISSN： 0933-5137  CODEN： MATWER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,高分子誘導セラミックルートにより合成したチタニア-シリコンオキシカーバイドナノ複合材料を,放電プラズマ焼結を用いて亀裂フリーモノリスに焼結し,それらの機械的特性ならびにそれらの見掛け密度を特性化した。X線回折図は,1200°Cで非晶質シリコンオキシカーバイドマトリックス中に10nm以下のサイズのアナターゼ相の安定化を明確に示した。ナノインデンテーションを用いて測定した硬度と弾性率はそれぞれ9GPaと82GPaであり,押込亀裂長さ法を用いて計算した破壊靱性は2.34MPam1/2であった。これに加え,ボールオン3ボール技法を用いて二軸曲げ強さを評価し,破壊メカニズムを理解するために破面検査を行った。Copyright 2022 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *機械的性質 ,  亀裂 ,  *焼結 ,  弾性係数 ,  破壊靱性 ,  非晶質 ,  高分子 ,  容積重 ,  二軸曲げ ,  アナターゼ ,  *放電プラズマ焼結
準シソーラス用語： 亀裂長さ ,  破壊機構 ,  *二酸化チタン ,  機械的特性評価 , 【Automatic Indexing@JST】

著者キーワード (8件)： 放電プラズマ焼結 ,  ナノインデンテーション ,  破壊靭性 ,  ボールオン3ボール法 ,  放電プラズマ焼結 ,  ナノインデンテーション ,  Bruchzaehigkeit ,  Vierkugel法

分類 (1件)： 圧粉,焼結  (WC02030X)

タイトルに関連する用語 (5件)： スパークプラズマ焼結 ,  チタニア ,  シリコンオキシカーバイド ,  ナノ複合材料 ,  機械的特性評価