Can oxygen vacancies in ceria surfaces be measured by O1s photoemission spectroscopy?

著者 (6件)： Bosio Noemi (Department of Physics, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Bosio Noemi (Competence Centre for Catalysis, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Schaefer Andreas (Competence Centre for Catalysis, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Schaefer Andreas (Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Gronbeck Henrik (Department of Physics, Chalmers University of Technology, SE-41296 Goteborg, Sweden) ,  Gronbeck Henrik (Competence Centre for Catalysis, Chalmers University of Technology, SE-41296 Goteborg, Sweden)
資料名： Journal of Physics. Condensed Matter  (Journal of Physics. Condensed Matter)
巻： 34  号： 17  ページ： 174004 (6pp)  発行年： 2022年 
JST資料番号： B0914B  ISSN： 0953-8984  CODEN： JCOMEL  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： X線光電子分光法は材料キャラクタリゼーションのための標準技術であり,O1s結合エネルギーは酸化物に対して一般的に測定される。ここでは,CeO_2(111)におけるO1s結合エネルギーが酸素空孔の存在によりどのように影響を受けるかを調べるために,密度汎関数理論計算を用いた。CeO_2(111)の点空格子点の場合をCe_2O_3への完全還元と比較した。酸素空孔によるCeO_2の還元は,O1s結合エネルギーにわずかな影響を有することが分かった。O1s結合エネルギーは,考察した酸素原子の化学結合の特性が,例えばOH基または炭酸塩の形成によって修正される時に,明らかに変化した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *光電子放出 ,  化学結合 ,  空格子点 ,  結合エネルギー ,  特性 ,  酸化物 ,  *酸化セリウム ,  炭酸塩 ,  ヒドロキシ基 ,  キャラクタリゼーション ,  X線光電子分光法
準シソーラス用語： *酸素空格子点 ,  酸素原子 ,  密度汎関数計算 , 【Automatic Indexing@JST】

分類 (1件)： 酸化物結晶の磁性  (BM06050E)

タイトルに関連する用語 (4件)： セリア ,  酸素空孔 ,  光電子放出 ,  分光法