強度-延性ジレンマを克服するロールボンド銅の粒界工学【JST・京大機械翻訳】

Grain boundary engineering in roll-bonded copper to overcome the strength-ductility dilemma

著者 (5件)： Taali Saeed (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Toroghinejad Mohammad Reza (Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111, Iran) ,  Toroghinejad Mohammad Reza (Faculty of Mechanical and Energy Engineering, Shahid Beheshti University, Tehran 16589-53571, Iran) ,  Kuglstatter Moritz (Materials Science and Engineering, Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Institute 1, Martensstr. 5, Erlangen, 91058, Germany) ,  Hoppel Heinz Werner (Materials Science and Engineering, Friedrich-Alexander-Universitaet Erlangen-Nuernberg (FAU), Institute 1, Martensstr. 5, Erlangen, 91058, Germany)
資料名： Journal of Materials Research and Technology  (Journal of Materials Research and Technology)
巻： 17  ページ： 3198-3204  発行年： 2022年 
JST資料番号： W3532A  ISSN： 2238-7854  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 傾斜および微細粒(FG)微細構造を有する銅シートを,累積圧延接合(ARB)とその後の焼鈍によって処理し,強度-延性関係に及ぼす構造的不均一性の影響を評価した。個々のARBプロセスステップの適切な設計によって,2種類の傾斜構造(GSs)が達成され,そこでは,粒径が,表面のより微細な結晶粒組織から内部(CGC)のより粗いもの,または内部(FGC)のより微細なものに,より粗いものへと徐々に変化した。両タイプに対して,粒径は,試料の厚さを横切って4~19ミクロンの間で徐々に変化した。均一引張仕事に関して,GSsはヘテロ変形誘起強化により強度と伸びの優れた組合せを示した。粗粒(CG)対応物と比較して,良好な歪非局在化能力に加えて,傾斜ミクロ組織は,不均一変形領域における亀裂経路に影響を及ぼす。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *延性 ,  変形 ,  *銅 ,  金属組織 ,  粒径 ,  伸び ,  引張 ,  傾斜 ,  強度
準シソーラス用語： 純銅 ,  不均一変形 ,  亀裂経路 ,  ロール圧接 ,  *粒界工学 ,  結晶粒組織 , 【Automatic Indexing@JST】

著者キーワード (4件)： 純銅 ,  ヘテロ構造材料 ,  勾配微細構造 ,  歪非局在化