酸化物セラミッククルーシブル中の一方向凝固二元Ti-49Al合金のラメラ配向制御と機械的性質【JST・京大機械翻訳】

Lamellae Orientation Control and Mechanical Properties of Directionally Solidified Binary Ti-49Al Alloy in Oxide Ceramics Crucible

著者 (12件)： Fan Jianglei (Henan Key Laboratory of Intelligent Manufacturing of Mechanical Equipment, School of Mechanical and Electrical Engineering, Zhengzhou University of Light Industry, Zhengzhou City, Henan Province, People’s Republic of China) ,  Fan Jianglei (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Wei Zexin (Henan Key Laboratory of Intelligent Manufacturing of Mechanical Equipment, School of Mechanical and Electrical Engineering, Zhengzhou University of Light Industry, Zhengzhou City, Henan Province, People’s Republic of China) ,  Li Ying (Henan Key Laboratory of Intelligent Manufacturing of Mechanical Equipment, School of Mechanical and Electrical Engineering, Zhengzhou University of Light Industry, Zhengzhou City, Henan Province, People’s Republic of China) ,  Li Ying (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Wang Yan (Henan Key Laboratory of Intelligent Manufacturing of Mechanical Equipment, School of Mechanical and Electrical Engineering, Zhengzhou University of Light Industry, Zhengzhou City, Henan Province, People’s Republic of China) ,  Wang Yan (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Wu Shen (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Zhou Xiangkui (Henan Key Laboratory of Intelligent Manufacturing of Mechanical Equipment, School of Mechanical and Electrical Engineering, Zhengzhou University of Light Industry, Zhengzhou City, Henan Province, People’s Republic of China) ,  Zhou Xiangkui (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Liu Jianxiu (Henan Engineering Research Center of Advanced Materials Processing and Testing, Zhengzhou University of Light Industry, Zhengzhou, People’s Republic of China) ,  Guo Jingjie (School of Material Science and Engineering, Harbin Institute of Technology, Harbin, People’s Republic of China)
資料名： International Journal of Metalcasting  (International Journal of Metalcasting)
巻： 16  号： 2  ページ： 622-633  発行年： 2022年 
JST資料番号： W4481A  ISSN： 1939-5981  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本論文では,酸化物セラミックるつぼ中の一方向凝固(DS)Ti-49Al(at%)合金のラメラ配向制御と機械的性質を調べた。核形成過冷却理論に基づいて,シード技術によるTi-49Al(at%)合金のラメラ配向制御のための実行可能な凝固パラメータを選択した。最適凝固パラメータは次の通りであった。成長速度(V)は10から25μm/sの範囲であり,温度勾配(G)は10から20K/mmの範囲であった。平行したラメラ配向を有するDS Ti-49Al(at%)合金を,予カチオン凝固パラメータに従って首尾よく調製した。DS Ti-49Al(at%)の機械的性質は,ラメラ構造の配向によって変化した。平行したラメラ配向を有する試料は比較的高い引張強度(450MPa)と伸び(0.60%)を示した。平行したラメラ配向を有する試料の機械的性質は,TiAlメルトと酸化物セラミックるつぼの間の界面反応によってわずかに汚染された試料であっても,等軸結晶粒構造の試料より大きかった。一方,DS Ti-49Al(at%)合金の破壊モードは,層間モード,トランスラメラモード,または2つのモードとの組み合わせであり,それはまた,ラメラ配向に依存した。グラフ抽象;Copyright American Foundry Society 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  過冷却 ,  *凝固 ,  *合金 ,  *一方向凝固 ,  不均一系反応 ,  層状組織 ,  結晶粒 ,  *坩堝 ,  引張強さ ,  温度勾配 ,  成長速度 ,  メルト
準シソーラス用語： 界面反応 ,  *配向制御 , 【Automatic Indexing@JST】

著者キーワード (5件)： TiAl金属間化合物 ,  一方向凝固 ,  微細構造制御 ,  ラメラ配向 ,  機械的性質

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： 酸化物セラミック ,  クルーシブル ,  一方向凝固 ,  Ti ,  ラメラ ,  配向制御 ,  機械的性質