変形誘起ナノスケール双晶は付加製造チタン合金における強度と延性を改善する【JST・京大機械翻訳】

Deformation induced nanoscale twinning improves strength and ductility in additively manufactured titanium alloys

著者 (5件)： Wang Pan (Singapore Institute of Manufacturing Technology, A*STAR, 73 Nanyang Drive, 637662, Singapore) ,  Tan Xipeng (Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117575, Singapore) ,  Nai Mui Ling Sharon (Singapore Institute of Manufacturing Technology, A*STAR, 73 Nanyang Drive, 637662, Singapore) ,  Wu Jiang (NanoAnalysis, Oxford Instruments Singapore, 3 Kaki Bukit Road 3, 417818, Singapore) ,  Wei Jun (Singapore Institute of Manufacturing Technology, A*STAR, 73 Nanyang Drive, 637662, Singapore)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 833  ページ： Null  発行年： 2022年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 電子ビーム融解(EBM)添加物製造法によって作製した種々のミクロ組織を有する航空宇宙グレードTi-6Al-4V部品の機械的性質を調べた。ミクロ組織のαラス幅は,EBM製Ti-6Al-4V試験片の変形機構に重要であることを見出した。変形誘起ナノスケール双晶は,約0.6μmの平均αラス幅を有する室温での高い加工硬化速度により観察され,それは,異常な延性を有する高い降伏強度と極限引張強度をもたらした。対照的に,平均αラス幅が約0.2~0.3μmの微細構造試験片は,低い加工硬化速度が発生し,転位塑性のみを示す。これらの知見は,相加的に製造されたTi-6Al-4Vにおける微細構造依存変形機構の詳細な理解を提供する。さらに重要なことに,本研究は,添加剤製造によるチタン合金における強度-延性トレードオフを克服することに光を当てる。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *延性 ,  加工硬化 ,  塑性 ,  機械的性質 ,  *双晶 ,  *チタン合金 ,  電子ビーム融解 ,  引張強さ ,  降伏強さ ,  *付加製造
準シソーラス用語： *ナノスケール ,  航空宇宙 ,  ナノ双晶 ,  変形機構 ,  三次元印刷 , 【Automatic Indexing@JST】

著者キーワード (4件)： ナノ双晶 ,  微細構造 ,  機械的性質 ,  3D印刷

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (6件)： 誘起 ,  ナノスケール ,  双晶 ,  付加製造 ,  チタン合金 ,  延性