金属ニッケル粒子の複合化によるLa_3-xTe_4における熱安定性と耐酸化性の向上【JST・京大機械翻訳】

Enhanced thermal stability and oxidation resistance in La_{3- x} Te₄ by compositing metallic nickel particles

著者 (14件)： Li Jian (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Li Jian (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China) ,  Liu Ruiheng (Institute of Advanced Materials Science and Engineering, Shenzhen Institutes of Advanced Technology, Chinese Academy of Sciences, Shenzhen 518055, China) ,  Song Qingfeng (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Gao Zhiqiang (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Huang Hui (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Huang Hui (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China) ,  Zhang Qihao (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Zhang Qihao (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China) ,  Shi Xun (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Bai Shengqiang (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Bai Shengqiang (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China) ,  Chen Lidong (State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China) ,  Chen Lidong (Center of Materials Science and Optoelectronics Engineering, University of Chinese Academy of Sciences, Beijing 100049, China)
資料名： Acta Materialia  (Acta Materialia)
巻： 224  ページ： Null  発行年： 2022年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： テルル化ランタン(La_3-xTe_4)は,1000K以上の高温で作動する熱電(TE)材料の重要な候補の1つである。しかし,TE材料の熱安定性と耐酸化性は,それらが高温で動作するとき,重要な問題になる。この報告で,La_3-xTe_4は不活性雰囲気下で1200Kまで優れた熱安定性を示すが,非常に低い分圧でも酸素の存在は700K以上の温度で重大な酸化と性能劣化を引き起こすことが分かった。La_2.74Te_4/Ni複合材料を形成するLa_2.74Te_4マトリックスに金属ニッケル粒子を導入することで,酸化速度は空気中と酸素分圧(Po_2=10-3MPa)の両方で大きく低下した。酸化中に形成された緻密なLa_2NiO_4/Ni_2Te_3O_8/NiO酸化物複合層は酸素の拡散を「ブロッキング」の電荷である。分散Ni粒子は,La_2.74Te_4/10vol.%Ni複合材料において1273Kで1.0として良好な無次元熱電性能指数をもたらす熱電特性に不明瞭な影響を与える。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 高温 ,  *酸化 ,  反応速度 ,  複合材料 ,  酸素 ,  *ニッケル ,  酸化物 ,  *耐酸化性 ,  熱安定性 ,  性能指数 ,  ブロッキング ,  電気特性 ,  分圧
準シソーラス用語： 酸素分圧 ,  酸化速度 ,  複合化 ,  熱電特性 ,  熱電性能指数 , 【Automatic Indexing@JST】

著者キーワード (5件)： 熱電 ,  テルル化ランタン ,  熱安定性 ,  ニッケル合成 ,  耐酸化性

分類 (3件)： 熱電デバイス  (NC03090J) ,  半導体結晶の電気伝導  (BM03043X) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (4件)： 金属ニッケル ,  複合化 ,  熱安定性 ,  耐酸化性