自立構造の3D印刷のための前面重合可能な形状記憶ポリマー【JST・京大機械翻訳】

Frontally polymerizable shape memory polymer for 3D printing of free-standing structures

著者 (4件)： An Yongsan (Department of Materials Science and Engineering and Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul 08826, Republic of Korea) ,  Jang Joon Hyeok (Department of Materials Science and Engineering and Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul 08826, Republic of Korea) ,  Youk Ji Ho (Department of Chemistry and Chemical Engineering, Education and Research Center for Smart Energy and Materials, Inha University, Incheon 22212, Republic of Korea) ,  Yu Woong-Ryeol (Department of Materials Science and Engineering and Research Institute of Advanced Materials (RIAM), Seoul National University, Seoul 08826, Republic of Korea)
資料名： Smart Materials and Structures  (Smart Materials and Structures)
巻： 31  号： 2  ページ： 025013 (11pp)  発行年： 2022年 
JST資料番号： W0480A  ISSN： 0964-1726  CODEN： SMSTER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 4次元(4D)印刷を用いて,時間とともに変化する特性を有する三次元(3D)プリント物体を記述した。形状記憶ポリマー(SMPs)は4D印刷技術の代表的材料である。SMPsと幾何学的に複雑な,自立型を印刷する能力は,4D印刷の成功に重要である。本研究では,ポリ(ジシクロペンタジエン)ネットワークにシクロオクテンを添加することにより,発熱性自己伝播を特徴とするSMPを合成できるSMPを合成し,スイッチングセグメントを得た。このSMPのレオロジー特性は,インキュベーション時間を調整することによって制御した。SMPを同時重合で印刷して自立構造を生成するように,ノズルシステムを設計した。印刷速度は,正面重合速度に従って3cm min-1に設定した。自立,六角形スパイラルを印刷し,印刷した螺旋構造は,約98%の固定比と100%の回収率で優れた形状記憶性能を示し,それによって,正面重合SMPの3D印刷性と形状記憶性能を示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： スイッチング ,  *印刷 ,  ネットワーク ,  印刷物 ,  *重合 ,  ヘリックス構造 ,  *形状記憶効果 ,  三次元 ,  発熱 ,  インキュベート ,  四次元
準シソーラス用語： *形状記憶ポリマ ,  レオロジー特性 ,  印刷技術 ,  *三次元印刷 , 【Automatic Indexing@JST】

分類 (1件)： 高分子固体の力学的性質  (CG02023D)

タイトルに関連する用語 (5件)： 自立 ,  3D印刷 ,  前面 ,  重合 ,  形状記憶ポリマー