高分子被覆のための簡易RAFTベース乳化重合プロセスによるJanus粒子【JST・京大機械翻訳】

Janus particles by simplified RAFT-based emulsion polymerization process for polymer coating

著者 (7件)： Nguyen Duc (Key Centre for Polymers and Colloids, School of Chemistry, University of Sydney Nano Institute, The University of Sydney, Sydney, NSW, Australia) ,  Huynh Vien T. (Key Centre for Polymers and Colloids, School of Chemistry, University of Sydney Nano Institute, The University of Sydney, Sydney, NSW, Australia) ,  Serelis Algirdas K. (DuluxGroup Australia, Clayton, VIC, Australia) ,  Davey Tim (DuluxGroup Australia, Clayton, VIC, Australia) ,  Paravagna Olga (DuluxGroup Australia, Clayton, VIC, Australia) ,  Such Chris H. (DuluxGroup Australia, Clayton, VIC, Australia) ,  Hawkett Brian S. (Key Centre for Polymers and Colloids, School of Chemistry, University of Sydney Nano Institute, The University of Sydney, Sydney, NSW, Australia)
資料名： Colloid and Polymer Science  (Colloid and Polymer Science)
巻： 300  号： 4  ページ： 341-349  発行年： 2022年 
JST資料番号： C0415A  ISSN： 0303-402X  CODEN： CPMSB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： RAFTベースのフリーラジカル乳化重合中の相分離により,膜形成高分子Janus粒子を合成する簡易法について述べた。完全に架橋したスノーマンまたはフットボール形状のポリスチレンJanus粒子(PSJP)を,安定剤として両親媒性トリブロックマクロ-RAFT共重合体を用いて1段階バッチプロセスで初めて製造した。水溶性開始剤の存在下で,メタクリル酸メチル(MMA)とアクリル酸ブチル(BA)(1/1重量)の単量体混合物を反応に常に注入する連続乳化重合において,そのような粒子をシードとして使用した。添加した単量体はシード粒子表面を濡れ,それらの重合は93nmの膜を形成し,単一または2ヘッドJanus粒子を形成した。得られたラテックスは,固体カルサイト延長剤を分散し,カプセル化するのに首尾よく使用された。グラフ抽象;Copyright The Author(s) 2022 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： ラジカル ,  バッチ処理 ,  ラテックス ,  重合開始剤 ,  相分離 ,  *乳化重合 ,  方解石 ,  安定剤 ,  単量体 ,  *高分子 ,  水溶性 ,  *固体粒子 ,  両親媒性
準シソーラス用語： 薄膜形成 ,  *Janus粒子 ,  高分子被覆 , 【Automatic Indexing@JST】

著者キーワード (4件)： カプセル化 ,  2頭雪人 ,  スノーマン ,  Janus粒子

分類 (2件)： コロイド化学一般  (CB11010C) ,  単独重合  (CG04020S)

タイトルに関連する用語 (5件)： 高分子被覆 ,  簡易 ,  RAFT ,  乳化重合プロセス ,  Janus粒子