常温におけるV添加物を含むZn-10Al合金のミクロ組織とクリープ挙動【JST・京大機械翻訳】

Microstructure and creep behaviour of Zn-10Al alloy with V additives at ambient temperature

著者 (6件)： Liu Xinyi (School of Materials Science and Engineering, Central South University, Changsha, Hunan 410083, PR China) ,  Liu Xinyi (Key Lab of Nonferrous Materials, Ministry of Education, Central South University, Changsha, Hunan 410083, PR China) ,  Lin Gaoyong (School of Materials Science and Engineering, Central South University, Changsha, Hunan 410083, PR China) ,  Lin Gaoyong (Key Lab of Nonferrous Materials, Ministry of Education, Central South University, Changsha, Hunan 410083, PR China) ,  Chen Mingming (School of Materials Science and Engineering, Central South University, Changsha, Hunan 410083, PR China) ,  Chen Mingming (Key Lab of Nonferrous Materials, Ministry of Education, Central South University, Changsha, Hunan 410083, PR China)
資料名： Materials Letters  (Materials Letters)
巻： 308  号： PA  ページ： Null  発行年： 2022年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 周囲温度でのZn-10Al合金のクリープ特性に及ぼすV合金化の影響を調べた。V合金化はZn-10Al結晶粒を著しく微細化し,新しいAl_3V相を観察した。冷間変形と熱処理の後,Zn-10Al-0.5V合金の定常状態クリープ速度は0.2≦σ_0.2と周囲温度で4.65×10-6h-1であり,V含有量の増加と共に減少した。Zn-10Al-0.5V合金は微細な結晶粒組織を持ち,分散したAl_3Vにより良好なクリープ抵抗を維持し,これは転位をピン止めし,粒界移動を妨げた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *クリープ ,  *合金 ,  熱処理 ,  バナジウム合金 ,  粒界移動 ,  結晶粒 ,  精密化 ,  クリープ速度
準シソーラス用語： 定常状態 ,  周囲温度 ,  *クリープ挙動 ,  クリープ特性 ,  耐クリープ性 ,  結晶粒組織 , 【Automatic Indexing@JST】

著者キーワード (4件)： V合金化 ,  Zn-10Al ,  微細構造 ,  クリープ

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 常温 ,  添加物 ,  Zn ,  ミクロ組織 ,  クリープ挙動