AlF_3→3H_2Oによるムライトホイスカ強化軽量多孔質材料の作製と特性評価【JST・京大機械翻訳】

Fabrication and characterization of mullite-whisker-reinforced lightweight porous materials with AlF₃・3H₂O

著者 (12件)： Deng Xiangong (Anhui Province Key Laboratory of Metallurgical Engineering & Resources Recycling (Anhui University of Technology), Ma’anshan, 243002, China) ,  Deng Xiangong (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Ji Peng (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Yin Jiaqiang (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Wang Yunlong (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Song Chenghao (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Li Saisai (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Zhang Yi (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China) ,  Ding Xiang (Anhui Province Key Laboratory of Metallurgical Engineering & Resources Recycling (Anhui University of Technology), Ma’anshan, 243002, China) ,  Ran Songlin (Anhui Province Key Laboratory of Metallurgical Engineering & Resources Recycling (Anhui University of Technology), Ma’anshan, 243002, China) ,  Zhang Haijun (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan, 430081, China) ,  Deng Hailiang (Key Laboratory of Green Fabrication and Surface Technology of Advanced Metal Materials, Ministry of Education, School of Materials Science and Engineering, Anhui University of Technology, Ma’anshan, 243032, China)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 10  ページ： 14891-14898  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ムライト-ホイスカ強化軽量多孔質材料を,フライアッシュと焼成ボーキサイトを原料とし,AlF_3・3H_2Oを添加剤として,粒子安定化法により調製した。ムライト-ホイスカ強化軽量多孔質材料の相組成,体積密度,多孔性,微細構造,機械的性能および熱伝導率に及ぼすAlF_3・3H_2Oの影響を調べた。AlF_3・3H_2O含有量の増加とともに,軽量多孔質材料の線形収縮,体積密度,圧縮強度,曲げ強度,および熱伝導率は増加し,それらの多孔性は減少した。AlF_3・3H_2O含有量が9wt%の時,気孔率72.3%,平均ホイスカ長さ約19.2μmの軽量多孔質材料試料の曲げと圧縮強度は,それぞれ17.8と31.0MPaであり,熱伝導率は0.092W(mK)-1の最小値で維持された。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 熱伝導率 ,  微細構造 ,  ボーキサイト ,  添加剤 ,  *ホイスカ ,  フライアッシュ ,  焼成 ,  相組成 ,  圧縮強さ ,  曲げ強さ ,  *ムライト ,  空隙率 ,  多孔質体
準シソーラス用語： 機械的性能 ,  軽量 , 【Automatic Indexing@JST】

著者キーワード (4件)： Lightweight porous materials ,  Mullite whisker ,  Mechanical performance ,  AlF₃・3H₂O

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (5件)： 強化 ,  軽量 ,  多孔質材料 ,  作製 ,  特性評価