FeCrNiMnAl_x高エントロピー合金の微細組織と摩耗特性に及ぼすAl含有量の影響【JST・京大機械翻訳】

Effect of Al content on microstructure and wear properties of FeCrNiMnAlx high-entropy alloys

著者 (4件)： Xing Xuewei (Institute of Advanced Wear & Corrosion Resistant and Functional Materials, Jinan University, Guangzhou 510632, Guangdong, People’s Republic of China) ,  Liu Ying (Institute of Advanced Wear & Corrosion Resistant and Functional Materials, Jinan University, Guangzhou 510632, Guangdong, People’s Republic of China) ,  Hu Jinkang (Institute of Advanced Wear & Corrosion Resistant and Functional Materials, Jinan University, Guangzhou 510632, Guangdong, People’s Republic of China) ,  Li Wei (Institute of Advanced Wear & Corrosion Resistant and Functional Materials, Jinan University, Guangzhou 510632, Guangdong, People’s Republic of China)
資料名： Materials Research Express  (Materials Research Express)
巻： 9  号： 3  ページ： 036510 (10pp)  発行年： 2022年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 一連のFeCrNiMnAl_x(x=0,0.3,0.5,0.8,1.0,モル比)高エントロピー合金(HEAs)を真空アーク融解法で調製した。ミクロ組織,機械的および摩耗特性に及ぼすAl含有量の影響を調べた。FeCrNiMn合金では,微細構造は面心立方(FCC)相を有する主要な均一構造であり,一方,FeCrNiMnAl_0.3はFCC+BCC+B_2相の混合物から成る樹枝状微細構造を生成し,Alのモル比が0.5を超えるとき,混合BCC+B_2樹枝状デンドライト間微細構造が現れた。HEAsの硬度と降伏応力はAl量の増加とともに効果的に改善されるが,延性は低下する。この場合,FeCrNiMnAl合金は延性の低下により降伏応力が低下した。さらに,摩擦係数は低下し,耐摩耗性はアルミニウム含有量の増加とともに改善された。FeCrNiMnAl_0.8HEAsは,強度と延性のバランスを達成する利点により,最良の耐摩耗性を有する。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  *合金 ,  耐摩耗性 ,  微細構造 ,  摩擦係数 ,  *アルミニウム ,  金属組織 ,  樹枝状結晶 ,  硬度 ,  降伏応力 ,  真空アーク ,  モル比 ,  *摩耗特性
準シソーラス用語： *高エントロピー合金 , 【Automatic Indexing@JST】

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 高エントロピー合金 ,  微細組織 ,  摩耗特性 ,  Al含有量