アセチル化修飾セルロースナノファイバー/ポリプロピレン複合材料の調製のための同時戦略【JST・京大機械翻訳】

A simultaneous strategy for the preparation of acetylation modified cellulose nanofiber/polypropylene composites

著者 (6件)： Duan Linjuan (Tianjin Key Laboratory of Pulp & Paper, Tianjin University of Science &Technology, Tianjin 300457, China) ,  Duan Linjuan (Yuncheng Vocational and Technical University, Yuncheng 044000, China) ,  Liu Rongrong (Tianjin Key Laboratory of Pulp & Paper, Tianjin University of Science &Technology, Tianjin 300457, China) ,  Duan Yan (Tianjin Key Laboratory of Pulp & Paper, Tianjin University of Science &Technology, Tianjin 300457, China) ,  Li Zhiqiang (Tianjin Key Laboratory of Pulp & Paper, Tianjin University of Science &Technology, Tianjin 300457, China) ,  Li Qun (Tianjin Key Laboratory of Pulp & Paper, Tianjin University of Science &Technology, Tianjin 300457, China)
資料名： Carbohydrate Polymers  (Carbohydrate Polymers)
巻： 277  ページ： Null  発行年： 2022年 
JST資料番号： E0961A  ISSN： 0144-8617  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,アセチル化修飾繊維(A-セルロース)のナノフィブリル化およびセルロースナノファイバー(CNF)/非極性ポリマー複合材料の調製による同時法を提案した。A-セルロースとイソタクチックポリプロピレン(iPP)を初めに混合し,次に二軸押出機中で溶融混練した。A-セルロース内部の水素結合力の低下と押出機による高剪断力により,PP複合材料(ACPP)の3次元ネットワークの状態に分布したアセチル化セルロースナノファイバ(A-CNF)が成功裏に調製された。A-CNFの走査電子顕微鏡(SEM)画像,動的機械分析(DMA)およびACPPのX線回折(XRD)結果は,A-CNFがPPマトリックスと良好な界面適合性を有し,PP結晶化を誘起し,結晶サイズを減少させ,複合材料中のγ結晶の比を増加させ,複合材料の機械的および熱力学的特性を改善することを示した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  界面 ,  結晶化 ,  水素結合 ,  走査電子顕微鏡 ,  ネットワーク ,  *アセチル化 ,  押出機 ,  三次元 ,  動的機械分析 ,  二軸押出機 ,  剪断力
準シソーラス用語： ナノフィブリル ,  溶融混練 ,  *セルロースナノファイバー , 【Automatic Indexing@JST】

著者キーワード (5件)： セルロースナノファイバー ,  アセチル化修飾 ,  ポリプロピレン ,  同時法 ,  複合材料

分類 (1件)： 多糖類  (CF10054P)