純銅の微細構造と性質に及ぼすCeCu_6とCu_2Sの影響【JST・京大機械翻訳】

Effects of CeCu₆ and Cu₂S on microstructure and properties in pure copper

著者 (27件)： Song Jin-tao (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Liu Hai-tao (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Liu Hai-tao (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Liu Hai-tao (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Song Ke-xing (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Song Ke-xing (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Song Ke-xing (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Song Ke-xing (Henan Academy of Sciences, Zhengzhou City, China) ,  Hua Yun-xiao (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Peng Xiao-wen (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Peng Xiao-wen (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Peng Xiao-wen (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  An Shi-zhong (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  An Shi-zhong (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  An Shi-zhong (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Cheng Chu (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Cheng Chu (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Cheng Chu (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Zhou Yan-jun (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Zhou Yan-jun (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Zhou Yan-jun (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Guo Xiu-hua (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Guo Xiu-hua (Henan Key Laboratory of Nonferrous Materials Science & Processing Technology, Luoyang City, China) ,  Guo Xiu-hua (Collaborative Innovation Center of Nonferrous Metals, Henan Province, Luoyang City, China) ,  Qiao Yu-bo (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Wang Guo-jie (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China) ,  Yang Lu-yao (School of Materials Science and Engineering, Henan University of Science and Technology, Luoyang City, China)
資料名： Journal of Materials Research and Technology  (Journal of Materials Research and Technology)
巻： 17  ページ： 1159-1166  発行年： 2022年 
JST資料番号： W3532A  ISSN： 2238-7854  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 純銅インゴット(CeとS元素,主にCeCu_6とCu_2Sの形で存在する)に300ppmのCeとS元素を添加したミクロ組織分析,電気伝導率試験,引張試験を利用し,鋳放し純銅のミクロ組織,電気伝導率,および機械的性質に及ぼすCeCu_6とCu_2Sの影響を調べた。その結果,鋳放し純銅,Cu-0.03CeおよびCu-0.03Sの平均粒径は,それぞれ,376,159および193μmであった。2相(CeCu_6とCu_2S)の結晶粒微細化機構は全く異なる。CeCu_6の結晶粒微細化機構は,主に成分過冷却に依存する。Cu_2Sの結晶粒微細化機構は粒成長の阻害に主に依存する。熱間押出の後,鋳放し純銅,Cu-0.03CeおよびCu-0.03Sの伝導率は,10.1,10.2および95.5から101.3,100.9および99.4%IACSに増加した。そして,伸びは,それぞれ66.59,49.17および34.23%であった。CeCu_6/Cu_2Sと銅マトリックス間の不一致は,それぞれ,10.24%(0210≦ε)_CeCu_6//(4σ′11)_Cu,24.91%(14≦δ612)_Cu_2S//(1σ*31)_Cuであった。CeCu_6と銅マトリックス間の不一致はCu_2Sと銅マトリックス間のそれよりも小さく,CeCu_6と銅マトリックス間の濡れ性,伝導率と界面結合強度が良かった。Cu-0.03Sの伝導率は熱間押出後に改善され,それは界面でのギャップが熱間押出によって部分的に減少できた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  過冷却 ,  機械的性質 ,  結晶成長 ,  電気伝導率 ,  引張試験 ,  *セリウム ,  *銅 ,  金属組織 ,  インゴット ,  伸び ,  結晶粒微細化 ,  熱間押出 ,  鋳放し
準シソーラス用語： *純銅 , 【Automatic Indexing@JST】

著者キーワード (6件)： 純銅 ,  CeCu_6 ,  Cu_2S ,  不登録 ,  微細構造 ,  機械的性質