HSS Q460DとQ690Dの高温機械特性の比較実験研究【JST・京大機械翻訳】

Comparative experimental studies of high-temperature mechanical properties of HSSs Q460D and Q690D

著者 (6件)： Wang Mengjie (School of Civil Engineering, Central South University, 68 South Shaoshan Road, Changsha 410075, China) ,  Wang Mengjie (School of Civil Engineering, Tongji University, Shanghai 200092, China) ,  Li Yaozhuang (School of Civil Engineering, Central South University, 68 South Shaoshan Road, Changsha 410075, China) ,  Li Guoqiang (State Key Laboratory for Disaster Reduction in Civil Engineering, Tongji University, Shanghai 200092, China) ,  Wang Weiyong (School of Civil Engineering, Chongqing University, Chongqing 400045, China) ,  Jiang Binhui (School of Civil Engineering, Central South University, 68 South Shaoshan Road, Changsha 410075, China)
資料名： Journal of Constructional Steel Research  (Journal of Constructional Steel Research)
巻： 189  ページ： Null  発行年： 2022年 
JST資料番号： D0026D  ISSN： 0143-974X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 460MPaと690MPa鋼の両方の試験データは,通常,それらの高温機械的性質において離散性を示した。本研究では,Q460DとQ690D鋼について,調和試験条件を用いて20°C~900°Cの温度範囲で比較実験研究を行い,異なる試験条件によって誘起される離散性を除去した。結果は,Q460DとQ690D鋼の間のf_1.0,f_1.5,およびf_2.0の降伏強度に対する減少因子の差は無視できることを示した。試験結果と電流基準の比較と利用可能な結果は,460MPaと690MPa鋼間の差が試験条件の影響を除外した後に著しく減少したことを示した。さらに,GB51249によって推奨されたf_1.0降伏強度は,BS5950によって推奨されたf_1.0およびf_1.5値,およびEC_3およびAISCによって推奨されたf_2.0値と同様に,Q460DおよびQ690D鋼の両方に適用可能である。さらに,高温におけるQ460DおよびQ690D鋼の機械的特性の低減因子を計算するための予測方程式を提案した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  *高温 ,  電流 ,  鋼 ,  降伏強さ ,  比較試験 ,  高強度鋼
準シソーラス用語： 温度範囲 ,  予測式 ,  米国鋼構造協会 ,  試験データ , 【Automatic Indexing@JST】

著者キーワード (4件)： 機械的性質 ,  高強度鋼 ,  高温 ,  還元因子

分類 (3件)： 金属構造  (RA04050W) ,  その他の構造材料による構造  (RA04060H) ,  コンクリート構造  (RA04030A)

タイトルに関連する用語 (3件)： 機械特性 ,  比較実験 ,  研究