柔軟な雲母基板上のエピタキシャル(110)配向La_0.7Sr_0.3MnO_3膜【JST・京大機械翻訳】

Epitaxial (110)-oriented La_0.7Sr_0.3MnO₃ film directly on flexible mica substrate

著者 (16件)： Ye Lianxu (College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, People’s Republic of China) ,  Ye Lianxu (MIIT Key Laboratory of Aerospace Information Materials and Physics (NUAA), Nanjing 211106, People’s Republic of China) ,  Zhang Di (School of Materials Engineering and School of Electrical and Computer Engineering, Purdue University, West Lafayette, IN 47907, United States of America) ,  Lu Juanjuan (School of Materials Engineering and School of Electrical and Computer Engineering, Purdue University, West Lafayette, IN 47907, United States of America) ,  Xu Sicheng (Jiangsu Key Laboratory of Thin Films, School of Physical Science and Technology, Soochow University, Suzhou 215006, People’s Republic of China) ,  Xu Ruixing (College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, People’s Republic of China) ,  Xu Ruixing (MIIT Key Laboratory of Aerospace Information Materials and Physics (NUAA), Nanjing 211106, People’s Republic of China) ,  Fan Jiyu (College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, People’s Republic of China) ,  Fan Jiyu (MIIT Key Laboratory of Aerospace Information Materials and Physics (NUAA), Nanjing 211106, People’s Republic of China) ,  Tang Rujun (Jiangsu Key Laboratory of Thin Films, School of Physical Science and Technology, Soochow University, Suzhou 215006, People’s Republic of China) ,  Wang Haiyan (School of Materials Engineering and School of Electrical and Computer Engineering, Purdue University, West Lafayette, IN 47907, United States of America) ,  Guo Haizhong (Key Laboratory of Material Physics, Ministry of Education, School of Physics and Microelectronics, Zhengzhou University, Zhengzhou 450052, People’s Republic of China) ,  Li Weiwei (College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, People’s Republic of China) ,  Li Weiwei (MIIT Key Laboratory of Aerospace Information Materials and Physics (NUAA), Nanjing 211106, People’s Republic of China) ,  Yang Hao (College of Science, Nanjing University of Aeronautics and Astronautics, Nanjing 211106, People’s Republic of China) ,  Yang Hao (MIIT Key Laboratory of Aerospace Information Materials and Physics (NUAA), Nanjing 211106, People’s Republic of China)
資料名： Journal of Physics. D. Applied Physics  (Journal of Physics. D. Applied Physics)
巻： 55  号： 22  ページ： 224002 (7pp)  発行年： 2022年 
JST資料番号： B0092B  ISSN： 0022-3727  CODEN： JPAPBE  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ペロブスカイト-雲母van der Waalsエピタクシーヘテロ構造の製作とキャラクタリゼーションは,フレキシブルデバイスの適用を実現するための重要なステップである。しかし,雲母基板上に成長したvan der Waalsエピタキシー構造の作製と研究は,今までに(111)配向ペロブスカイト機能性酸化物薄膜に限られ,バッファ層が非常に必要である。本研究では,バッファ層を使用せずに雲母基板上にLa_0.7Sr_0.3MnO_3(LSMO)薄膜を直接成長させた。x線回折と走査型透過電子顕微鏡のキャラクタリゼーションにより,雲母基板上の(110)配向LSMO薄膜のエピタキシャル成長を示した。van der Waalsエピタキシーにより雲母基板上に成長したLSMO薄膜は従来の格子整合エピタキシーの代わりにドメイン整合エピタキシーを採用した。LSMO薄膜と雲母基板の間の2種類のドメイン整合関係を,電子と構造分析ソフトウェアの可視化によってスケッチし,議論した。(110)配向LSMO薄膜には,偏心強磁性が保持された。本研究は,フレキシブル雲母基板上に(110)配向機能性酸化物薄膜を作製する新しい経路を示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *エピタクシー ,  回折 ,  基板 ,  強磁性 ,  薄膜 ,  構造解析 ,  酸化物 ,  可視化 ,  *雲母 ,  素子構造 ,  ソフトウェア ,  バッファ層 ,  格子整合
準シソーラス用語： ドメイン構造 ,  ヘテロ構造 ,  酸化物薄膜 ,  フレキシブルデバイス , 【Automatic Indexing@JST】

分類 (2件)： 酸化物結晶の磁性  (BM06050E) ,  電気物性一般  (BM03010R)

タイトルに関連する用語 (3件)： 雲母 ,  エピタキシャル ,  配向