新しいニッケル基粉末超合金の微細構造安定性に及ぼす長期時効の影響【JST・京大機械翻訳】

Effect of long-term aging on microstructure stability of a novel nickel base powder superalloy

著者 (5件)： Yang Guohui (School of Materials Science and Engineering, University of Science and Technology, Beijing 100083, China) ,  Tian Gaofeng (Science and Technology on Advanced High Temperature Structure Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China) ,  Zhang Xianliang (School of Materials Science and Engineering, University of Science and Technology, Beijing 100083, China) ,  Gao Kewei (School of Materials Science and Engineering, University of Science and Technology, Beijing 100083, China) ,  Ji Zhen (School of Materials Science and Engineering, University of Science and Technology, Beijing 100083, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 906  ページ： Null  発行年： 2022年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 800°Cで100h~10000h時効したニッケル基粉末超合金の炭化物と有害な相TCPのミクロ組織安定性,進展則,および同定を,電界放出走査電子顕微鏡,原子間力顕微鏡,および電子後方散乱回折によって研究した。その結果,時効時間の増加とともに,粒径はほとんど変化せず,結晶粒界は粗大化し,そして,双晶境界Σ3は,最初に増加して,次に,減少し,そして,次に,γ′相は,最初に増加し,そして,次に,粗大化速度は,主に,AFM分析による隣接γ′相の組合せであった。1000h時効後,Lath様σ相CrCoは結晶粒界に最初に析出した。時効時間が2000時間まで,針状μ相Co_7(W,Mo)_6が結晶中に観察された。時効時間の更なる増加によって,結晶粒界と結晶におけるTCP相の総含有量は明らかに増加した。しかし,10000hでは,主にTCP相の原子がγ′相に拡散し,新しい固溶体を形成し,結晶粒界に堆積し,さらに結晶粒界を粗大化させるため,結晶と結晶粒界のTCP相はほとんど消失した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶粒界 ,  固溶体 ,  *時効 ,  *粉体 ,  金属組織 ,  炭化物 ,  σ相 ,  双晶境界 ,  *超合金 ,  γ相 ,  中間相 ,  μ相 ,  γプライム相 ,  原子間力顕微鏡
準シソーラス用語： 電界放出型走査電子顕微鏡 ,  TCP相 , 【Automatic Indexing@JST】

著者キーワード (5件)： ニッケル基粉末超合金 ,  長期老化 ,  γγ相 ,  TCP位相同定 ,  微細構造安定性

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： ニッケル基 ,  粉末 ,  超合金 ,  微細 ,  構造安定性 ,  長期 ,  時効