水蒸気種による極超音速プラズマ中の炭化ケイ素の加速腐食【JST・京大機械翻訳】

Accelerated corrosion of silicon carbide in hypersonic plasmas with water vapor species

著者 (6件)： Zhao Changhao (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China) ,  Yang Lingwei (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China) ,  Xiao Xueren (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China) ,  Wang Guolin (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China) ,  Zhang Jun (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China) ,  Luo Jie (Hypervelocity Aerodynamics Institute, China Aerodynamics Research and Development Center, Mianyang, 621000, China)
資料名： Ceramics International  (Ceramics International)
巻： 48  号： 2  ページ： 2886-2892  発行年： 2022年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,誘導結合プラズマ風洞における極超音速水蒸気プラズマを発生させるための新しい方法を提案した。それに基づいて,典型的なSiC被覆の酸化挙動を,減圧における熱流束を変えて研究した。重要な観察は,水蒸気プラズマ中の<1300°CでのSiC被覆の加速腐食であり,さらに,グラファイト基板からの早期破断を引起こした。破壊温度は,純粋な空気プラズマにおけるものよりはるかに低かった。腐食機構を,空気と水蒸気プラズマの両方における酸化挙動を比較することによって議論した。SiC腐食は,主に,形成されたSiO_2の水蒸気種との反応性の結果であった。その結果,熱平衡は酸化表面ではほとんど達成されず,酸化温度は変動した。腐食が水蒸気プラズマ中で進行するにつれて,SiC被覆は,最終的にはグラファイトのアブレーションにより剥離した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 酸化 ,  *プラズマ ,  *腐食 ,  破断 ,  熱流束 ,  被覆 ,  腐食機構 ,  グラファイト ,  *炭化ケイ素 ,  熱平衡 ,  電磁結合 ,  アブレーション
準シソーラス用語： *超音速 ,  酸化挙動 ,  水蒸気プラズマ , 【Automatic Indexing@JST】

著者キーワード (4件)： 極超音速機 ,  アクティブ冷却TPS ,  水蒸気酸化 ,  腐食機構

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  溶射  (WC08030N)

タイトルに関連する用語 (5件)： 水蒸気 ,  プラズマ ,  炭化ケイ素 ,  加速 ,  腐食