柱状から等軸への転移と結晶粒微細化を促進することによるβ-fleck欠陥フリー付加製造チタン合金に向けて【JST・京大機械翻訳】

Towards β-fleck defect free additively manufactured titanium alloys by promoting the columnar to equiaxed transition and grain refinement

著者 (4件)： Ng C.H. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD, 4072, Australia) ,  Bermingham M.J. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD, 4072, Australia) ,  Yuan L. (Department of Mechanical Engineering, University of South Carolina, Columbia, SC 29201, United States) ,  Dargusch M.S. (Centre for Advanced Materials Processing and Manufacturing, School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD, 4072, Australia)
資料名： Acta Materialia  (Acta Materialia)
巻： 224  ページ： Null  発行年： 2022年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Crのような偏析したβ安定化元素の高い含有量を含む準安定β-Titanium合金は,凝固処理中に回避するのが困難な偏析欠陥(β-flecksまたはβ-frecklesとして知られている)を形成する。本研究では,Wire Arc添加剤製造によって製造された高強度Ti-3Al-8V-6Cr-4Mo-4Zr(Beta-C/ASTMグレード19)におけるβ-フレックの形成を調べ,合金への結晶粒微細化剤(La_2O_3)の導入が偏析欠陥を成形から防止できるかどうかを調査した。柱状から等軸への転移およびLa_2O_3核形成粒子による粒径の微細化は,非精錬(標準)合金と比較して,β-フレックの存在を99.9%まで著しく減少させることが分かった。解析的および数値的モデリングを用いて,結晶粒微細化がこの顕著な欠陥減少を達成できる方法に関する洞察を与えた。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  凝固 ,  *合金 ,  偏析 ,  添加剤 ,  クロム ,  *チタン合金 ,  精錬 ,  粒径 ,  モデリング ,  *結晶粒微細化 ,  精密化 ,  *付加製造
準シソーラス用語： ミクロ偏析 ,  結晶粒微細化剤 , 【Automatic Indexing@JST】

著者キーワード (4件)： チタン合金 ,  ミクロ偏析 ,  結晶粒微細化 ,  欠陥