CoFeV_0.5Mn_0.5Siの電子バンド構造と磁性【JST・京大機械翻訳】

Electronic band structure and magnetism of CoFeV_0.5Mn_0.5Si

著者 (8件)： Kharel Parashu (Department of Physics, South Dakota State University, Brookings, South Dakota 57007, USA) ,  Baker Gavin (Department of Physics, South Dakota State University, Brookings, South Dakota 57007, USA) ,  Flesche Matthew (Department of Physics, South Dakota State University, Brookings, South Dakota 57007, USA) ,  Ramker Adam (Department of Physics, University of Northern Iowa, Cedar Falls, Iowa 50614, USA) ,  Moua Young (Department of Physics, University of Northern Iowa, Cedar Falls, Iowa 50614, USA) ,  Valloppilly Shah (Nebraska Center for Materials and Nanoscience, University of Nebraska, Lincoln, Nebraska 68588, USA) ,  Shand Paul M. (Department of Physics, University of Northern Iowa, Cedar Falls, Iowa 50614, USA) ,  Lukashev Pavel V. (Department of Physics, University of Northern Iowa, Cedar Falls, Iowa 50614, USA)
資料名： AIP Advances (Web)  (AIP Advances (Web))
巻： 12  号： 3  ページ： 035011-035011-5  発行年： 2022年 
JST資料番号： U7121A  ISSN： 2158-3226  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 半金属ホイスラー合金は,スピン輸送ベースデバイスへの応用の可能性により,大きな注目を集めている。600°Cで24時間アーク融解と高真空アニーリングを用いて,そのような合金CoFeV_0.5Mn_0.5Siを合成した。第一原理計算から,CoFeV_0.5Mn_0.5Siは,約93%のスピン分極度を持つほぼ半金属バンド構造を示した。さらに,この値は引張歪の適用によって強化できる。室温X線回折パターンを二次相のない立方晶結晶構造で指数付けした。アニールした試料は室温(T_c=657K)以上のCurie温度と約92emu/gの飽和磁化を持つ強磁性秩序を示した。著者らの結果は,CoFeV_0.5Mn_0.5Siが室温スピン輸送ベースデバイスに対する可能性を有することを示した。Copyright 2022 AIP Publishing LLC All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Curie温度 ,  合金 ,  焼なまし ,  *バンド構造 ,  飽和磁化 ,  スピン分極 ,  計算 ,  立方晶系 ,  半金属 ,  磁気秩序 ,  アーク融解 ,  *磁性 ,  ホイスラー合金
準シソーラス用語： スピン輸送 ,  第一原理計算 ,  引張歪 ,  強磁性秩序 , 【Automatic Indexing@JST】