無樹枝状リチウム堆積のためのアニオン親和性金属有機骨格によるアニオン枯渇領域の除去とLi+溶媒和の促進【JST・京大機械翻訳】

Eliminating anion depletion region and promoting Li⁺ solvation via anionphilic metal organic framework for dendrite-free lithium deposition

著者 (15件)： Li Yaoyao (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Liu Yuanpeng (National Key Laboratory of Science and Technology on Advanced Composites in Special Environments, and Center for Composite Materials and Structures, Harbin Institute of Technology, Harbin 150080, China) ,  Xue Lanxin (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Chen Wei (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Lei Tianyu (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Hu Anjun (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Huang Jianwen (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Wang Xuepeng (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Wang Xianfu (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Chen Bo (Institute of Microelectronics of Chinese Academy of Sciences, Beijing 100029, China) ,  Hu Yin (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Hu Yin (School of Materials and Energy, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Yang Chengtao (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China) ,  Yang Chengtao (Yangtze Delta Region Institute (Huzhou), University of Electronic Science and Technology of China, Huzhou 313001, China) ,  Xiong Jie (State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China)
資料名： Nano Energy  (Nano Energy)
巻： 92  ページ： Null  発行年： 2022年 
JST資料番号： W3116A  ISSN： 2211-2855  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： リチウム金属電池(LMB)は,多様な陰極材料と結合した高い理論容量と理想的な適合性により次世代再充電可能電池に大きな可能性を有する。しかし,アニオンとカチオン間の静電力によって誘起されたLi+溶媒和過程に関連するLi+の不十分な還元と同様に,アノード表面近傍のアニオン枯渇に起因する大きな局所空間電荷に関連したランダムLi析出は,高エネルギー密度LMBの開発を妨げる。ここでは,理論的および実験的に証明されたように,アニオン枯渇領域を同時に除去し,アニオン分布を制御し,Li+とのその結合を弱めるために,アニオン親和性添加剤として不飽和金属部位を有するZIF-67を用いて,リチウム塩解離を促進した。その結果,短回路ハザードは,2000時間以上3mAh cm-2の容量の下で3mAcm-2の修飾電解質を有する対称セルで再送られる。4.5mgcm-2の高い硫黄負荷を有するリチウム-硫黄電池に採用されたように,変調した電解質は,電池を3mAcm-2で100サイクルにわたってサイクル当たり0.05%の減衰速度で713mAhg-1の初期容量を供給できる。本研究は,アニオン枯渇領域を除去し,Li+溶媒和プロセスを促進することにより,デンドライトフリーLMBを構築するための効率的でスケーラブルな戦略を実証した。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 対称性 ,  電池 ,  *リチウム ,  *溶媒和 ,  電解質 ,  *アニオン ,  カチオン ,  硫黄 ,  *親和性 ,  アノード
準シソーラス用語： 静電気力 ,  リチウム塩 ,  再充電 ,  リチウム硫黄電池 ,  *MOF【配位高分子】 , 【Automatic Indexing@JST】

著者キーワード (4件)： リチウム金属アノード ,  金属有機骨格 ,  アニオン枯渇 ,  Li+溶媒和

分類 (1件)： 二次電池  (YB04030K)

タイトルに関連する用語 (8件)： リチウム ,  堆積 ,  アニオン ,  親和性 ,  金属有機骨格 ,  枯渇 ,  溶媒和 ,  促進