動的圧縮下のZK60合金における双晶と転位の相互作用【JST・京大機械翻訳】

Interactions between twins and dislocations in ZK60 alloy under dynamic compression

著者 (16件)： Zhou Le (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Zhou Le (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Li Yutian (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Li Yutian (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  He Zhenyu (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  He Zhenyu (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Wang Zhi (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Wang Zhi (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Liu Shimeng (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Liu Shimeng (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Wang Feng (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Wang Feng (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Mao Pingli (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Mao Pingli (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Liu Zheng (School of Materials Science and Engineering, Shenyang University of Technology, Shenyang, People’s Republic of China) ,  Liu Zheng (Key Laboratory of Magnesium Alloys and the Processing Technology of Liaoning Province, Shenyang University of Technology, Shenyang, People’s Republic of China)
資料名： Materials Science and Technology  (Materials Science and Technology)
巻： 38  号： 6  ページ： 342-351  発行年： 2022年 
JST資料番号： C0304C  ISSN： 0267-0836  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 動的圧縮下のZK60合金の[数式:原文を参照]引張双晶と転位間の相互作用を電子後方散乱回折と透過電子顕微鏡により調べた。試料は2つのグループに分けられ,グループ1は,異なる歪(4,6,9,12%)で一次変形を経験し,グループ2は一次変形(4%+8%,6%+6%,9%+3%)に基づく二次変形を経験し,12%の最終変形に達した。その結果,[数式:原文を参照]引張双晶は変形の初期段階における支配的な変形機構であり,[数式:原文を参照]引張双晶と転位密度の体積率は変形の増加とともに増加することが明らかになった。さらに,一次変形中に発生する双晶境界と転位は二次変形中の転位運動に対する抵抗になる。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  *相互作用 ,  *双晶 ,  *転位【結晶】 ,  *マグネシウム合金 ,  双晶境界 ,  転位密度 ,  引張 ,  機構 ,  *動的圧粉 ,  透過型電子顕微鏡 ,  体積率
準シソーラス用語： *ZK60 ,  EBSD ,  変形機構 ,  転位運動 , 【Automatic Indexing@JST】

著者キーワード (4件)： ZK60合金 ,  動的圧縮 ,  双生児 ,  転位

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： 動的圧縮 ,  ZK60 ,  合金 ,  双晶 ,  転位 ,  相互作用