熱間変形中の核グレード316Hステンレス鋼における動的再結晶の遷移挙動【JST・京大機械翻訳】

Transitional Behavior for Dynamic Recrystallization in Nuclear Grade 316H Stainless Steel during Hot Deformation

著者 (5件)： Wang Zhiguo (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, China) ,  Gao Fei (Key Laboratory of Lightweight Structural Materials, Liaoning Province, School of Materials Science and Engineering, Northeastern University, Shenyang, China) ,  Zhang Weina (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, China) ,  Cao Guangming (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, China) ,  Liu Zhenyu (State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang, China)
資料名： Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science  (Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science)
巻： 53  号： 2  ページ： 523-534  発行年： 2022年 
JST資料番号： E0265B  ISSN： 1073-5623  CODEN： MTTABN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 種々のZener-Hollomon(Z)値を有する熱間変形中の動的再結晶(DRX)挙動と変態プロセスを,核グレード316Hステンレス鋼において調べ,DRX変態,特に断熱加熱に影響する因子を深さで評価した。熱間変形の間,Z値の増加によって,流動軟化(DFS)の等級は,最初に減少して,次に段階的に増加した傾向を示した。微細構造の解析は,低Z値(3.9×1019s-1を超える)変形条件において,DRXは塊状に活性化され,再結晶機構はZ値の増加と共に連続DRX(CDRX)から不連続DRX(DDRX)への遷移を持ち,均一結晶粒の不均一結晶粒への転移をもたらすことを明らかにした。さらに,高Z値変形条件でのDRXの再活性化により,不連続DRXが一次再結晶モードになった。断熱加熱は,低温あるいは高歪速度(高Z値,6.1×1021s-1)の熱間変形中のDRXと流動軟化の再活性化の促進に重要な役割を果たす。Copyright The Minerals, Metals & Materials Society and ASM International 2021. corrected publication 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *再結晶 ,  低温 ,  微細構造 ,  *ステンレス鋼 ,  結晶粒 ,  歪速度 ,  不連続性 ,  *動的再結晶
準シソーラス用語： 一次再結晶 ,  再活性化 ,  核グレード , 【Automatic Indexing@JST】

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： 核グレード ,  ステンレス鋼 ,  動的再結晶 ,  遷移 ,  挙動