動的ジスルフィド結合と多重水素結合を含むポリウレタン減衰エラストマの調製と分子動力学研究【JST・京大機械翻訳】

Preparation and molecular dynamics study of polyurethane damping elastomer containing dynamic disulfide bond and multiple hydrogen bond

著者 (8件)： Xiaolin Jiang (South China University of Technology, Guangzhou 510641, China) ,  Min Xu (South China University of Technology, Guangzhou 510641, China) ,  Minhui Wang (South China University of Technology, Guangzhou 510641, China) ,  Yuanhao Ma (South China University of Technology, Guangzhou 510641, China) ,  Wencong Zhang (South China University of Technology, Guangzhou 510641, China) ,  Yanan Zhang (South China University of Technology, Guangzhou 510641, China) ,  Haoxiang Rong (South China University of Technology, Guangzhou 510641, China) ,  Xun Lu (South China University of Technology, Guangzhou 510641, China)
資料名： European Polymer Journal  (European Polymer Journal)
巻： 162  ページ： Null  発行年： 2022年 
JST資料番号： B0690A  ISSN： 0014-3057  CODEN： EUPJA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 減衰材料の使用は,振動と騒音を制御する有効な対策であり,広く使われる。しかし,減衰と機械的性質のバランスを見出すため,高分子減衰材料は比較的困難である。ここでは,ポリウレタンを,ジレンマに対処するために,異なる強度の動的なジスルフィド結合と水素結合を含むように設計した。ポリウレタンは,良好な減衰および機械的性質(有効減衰温度範囲17°Cおよび引張強度14.98±0.50MPa)を与えた。分子動力学を動的機械分析(DMA)と広帯域誘電緩和分光法(BDRS)を組合せて研究した。ミクロ相分離形態と分離度を用いて,分子動力学を説明した。ソフト相のセグメント運動は,ガラス転移温度(T_g)において困難になり,2, 2′-ジチオジ安息香酸(DTSA)含有量の増加とともに高温においてより速くなった。これらの結果は,減衰性能の改善機構を説明し,将来の減衰材料を設計するためのいくつかの参照を提供する。Copyright 2022 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 高温 ,  *水素結合 ,  騒音 ,  *ポリウレタン ,  ガラス転移点 ,  *ジスルフィド結合 ,  高分子 ,  *多重化 ,  引張強さ ,  広帯域 ,  *分子動力学 ,  動的機械分析 ,  ミクロ相分離
準シソーラス用語： 温度範囲 ,  *エラストマ , 【Automatic Indexing@JST】

著者キーワード (5件)： ポリウレタン ,  ジスルフィド結合 ,  水素結合 ,  ミクロ相分離 ,  構造と性能

分類 (2件)： 高分子固体の構造と形態学  (CG02022M) ,  機械的性質  (YH02022L)

タイトルに関連する用語 (9件)： ジスルフィド結合 ,  多重 ,  水素結合 ,  ポリウレタン ,  減衰 ,  エラストマ ,  調製 ,  分子動力学 ,  研究